Process of manufacturing polyols

ABSTRACT

A method of producing a polyether polyol includes reacting a low molecular weight initiator with ethylene oxide in the presence of a polymerization catalyst, and the low molecular weight initiator has a nominal hydroxyl functionality at least 2. The polymerization catalyst is a Lewis acid catalyst having the general formula M(R1)1(R2)1(R3)1(R4)0 or 1, whereas M is boron, aluminum, indium, bismuth or erbium, R1, R2, R3, and R4 are each independent, R1 includes a fluoroalkyl-substituted phenyl group, R2 incudes a fluoroalkyl-substituted phenyl group or a fluoro/chloro-substituted phenyl group, R3 includes a fluoroalkyl-substituted phenyl group or a fluoro/chloro-substituted phenyl group, and optional R4 includes a functional group or functional polymer group, R1 being different from at least one of R2 and R3.

FIELD

Embodiments relate to methods of manufacturing polyols using at least a Lewis acid catalyst, polyols prepared using at least the Lewis acid catalyst, and/or polyurethane products prepared using the polyols prepared using at least the Lewis acid catalyst.

INTRODUCTION

Polyether polyols are produced by polymerizing an alkylene oxide in the presence of a starter compound and a catalyst. The starter compound has one or more functional groups the alkylene oxide can react with to begin forming polymer chains. The starter compound may influence the molecular weight and establish the number of hydroxyl groups that the resultant polyether polyol will have.

With respect to the catalyst for forming polyether polyols, manufacturing is moving toward the use of a double-metal cyanide (DMC) catalyst in place of an alkali metal catalyst (such as a KOH based catalyst). A disadvantage of DMC catalysts is that they may activate slowly, as is taught in U.S. Pat. No. 9,040,657. In particular, preparation of polyether polyols using the DMC catalyst may begin with a stage of the reaction known as the catalyst induction period. During this stage of the reaction, the DMC catalyst is believed to become converted in situ from an inactive form into a highly active form that rapidly polymerizes the alkylene oxide as long as the catalyst remains active. This catalyst induction period is typically an indeterminate period of time following the first introduction of alkylene oxide to the reactor. It is common to introduce a small amount of alkylene oxide at the start of the polymerization process and then wait until the catalyst has become activated (as indicated, e.g., by a drop in reactor pressure due to the consumption of the initial alkylene oxide that had been charged into the reactor) before continuing with the alkylene oxide feed. Very little or no polymerization occurs until the catalyst has become activated, such that long activation times have a direct negative impact on the productivity of the process. It is sometimes the case that the catalyst does not become activated at all. Such a failure of the catalyst to activate may result in the abandonment of the attempt, and the process is started over again from the beginning. As such, the activation process results in some loss of productivity under the best circumstances, and under the worst circumstances can cause a loss of the entire batch of starting mixture. Thus, the reduction or elimination of the induction period at the start of the alkoxylation reaction is seen to be highly desirable.

The disadvantages of the use of conventional Lewis acids such as boron trifluoride to polymerize epoxides is well-known, e.g., as taught in U.S. Pat. No. 6,624,321. For example, use of such conventional Lewis acids as catalysts may lead to the formation of volatile low molecular weight cyclic ethers, may require high levels of catalyst loading (which ultimately require the need for a later process stage to remove catalyst from the resultant product), and may lead to catalyst decomposition during which release of a highly corrosive HF side-product and incorporation of fluorine atoms in the backbone of the polymerization product may occur. Further, boron trifluoride is regarded as hazardous material that is also moisture sensitive and difficult to handle.

The use of tris(pentafluorophenyl)borane catalyst during ring-opening polymerization of an alkylene oxide is taught, e.g., in U.S. Pat. No. 6,531,566. The tris(pentafluorophenyl)borane catalyst provides several advantages over conventional Lewis acids such as boron trifluoride. For example, the tris(pentafluorophenyl)borane catalyst is not corrosive, easy to handle, and appreciably more active. However, tris(pentafluorophenyl)borane catalyst produces an undesirable side-reaction leading to formation of aldehydes and acetal linkages in the polyol backbone.

The use of a dual catalyst package for producing a polyol having a high primary hydroxyl group content, which includes a DMC catalyst and a Lewis acid catalyst such as tris(pentafluorophenyl)borane is disclosed, e.g., in International Publication No. WO 2016/064698. The DMC catalyst enables the production of high molecular weight segments efficiently and the Lewis acid catalyst enables the formation of primary hydroxyl end groups. This method may minimize the residence time of the Lewis acid step and therefore the amount of side-product.

A method of using a combination of DMC and KOH catalysts to produce EO-capped polyether polyols is taught, e.g., in U.S. Patent Publication No. 2011/0230581. In this process, the DMC catalyst is utilized to polymerize propylene oxide (PO) and KOH catalyst is utilized to promote ethylene oxide (EO) capping. This technology suffers from all the drawbacks of conventional KOH technology, such as slow kinetics and need for catalyst removal or finishing steps in the resultant polyether polyols.

A method of using a combination of tris(pentafluorophenyl)borane (Lewis acid) and KOH catalysts to product EO-capped polyether polyols is taught in, e.g., U.S. Pat. No. 9,388,271. In this process, the tris(pentafluorophenyl)borane catalyst is utilized to polymerize PO in a first step. During the first step, the vapor phase in the autoclave is circulated through a reaction column and distillation column and back to the autoclave reactor in order to minimize side-product formation. In a second step, the KOH catalyst is utilized to polymerize EO onto the PO chain ends. This process is complicated and may require finishing step(s) to remove KOH catalyst residues.

Therefore, improvements are sought with respect to producing EO based polyols (such as EO-capped polyols) efficiently in such a way so as to not require a catalyst removal step and/or to changing the selectivity of the Lewis acid catalyst itself, e.g., to improve yield of the desired ethylene oxide-based polyether polyol product (such as the EO capped polyether polyol having a number molecular weight of at least 224 g/mol and EO capping of at least 1 wt % based on a total weight of the resultant polyether polyol). Accordingly, improvements are sought with respect to improving yield of desired products and/or producing non-finishing polyols (i.e., polyols that do not require further finishing).

SUMMARY

Embodiments may be realized by providing a method of producing a polyether polyol includes reacting a low molecular weight initiator with ethylene oxide in the presence of a polymerization catalyst, and the low molecular weight initiator has a nominal hydroxyl functionality at least 2. The polymerization catalyst is a Lewis acid catalyst having the general formula M(R¹)₁(R²)₁(R³)₁(R⁴)_(0 or 1), whereas M is boron, aluminum, indium, bismuth or erbium, R¹, R², R³, and R⁴ are each independent, R¹ includes a first fluoroalkyl-substituted phenyl group, R² incudes a second fluoroalkyl-substituted phenyl group or a first fluoro/chloro-substituted phenyl group, R³ includes a third fluoroalkyl-substituted phenyl group or a second fluoro/chloro-substituted phenyl group, and optional R⁴ includes a functional group or functional polymer group, R¹ being different from at least one of R² and R³. The method further includes forming a polyether polyol having a number average molecular weight of greater than the number average molecular weight of the low molecular weight initiator in the presence of the Lewis acid catalyst.

DETAILED DESCRIPTION

Ethylene oxide (EO) is an important and widely used monomer in the production of polyether polyols. EO polymerization offers the opportunity to significantly increase the reactivity of polyol with polyisocyanates relative to PO polyols by virtue of the resulting primary hydroxyl end groups. Homopolymers of EO such as certain polyethylene glycols, may find limited use in polyurethanes as they may crystallize readily and/or have a high affinity to water. The high affinity of polyethylene glycols to water may be detrimental to the properties of resultant polyurethanes products, e.g., as the products may be sensitive to the humidity in the environment. The use of block structures formed by the addition of short EO segments (referred to as EO capping) to PO and/or BO polyols has been proposed as a compromise between increasing reactivity with isocyanates and minimizing difficulties associated with processability and water affinity. Another approach is to copolymerize EO and PO and/or BO (e.g., mixed feed polyols) to form polyols that are composed of statistical mixtures of EO and PO and/or BO. From a reactivity point of view, the highest primary hydroxyl content and therefore reactivity may be achieved using the capping approach.

Currently, EO-capped polyols on an industrial scale are typically produced utilizing KOH-catalyzed polymerization technology. Also, many have found that DMC catalysts are typically unable to efficiently polymerize EO at a commercial scale. The use of conventional Lewis acids to polymerize EO is not preferred due to side-reactions. For example, these side-reaction may result in volatile side-products such as small cyclic ethers and acetaldehyde. As a result, the yield of the reaction may be greatly diminished. In addition, extra purification steps may be needed to obtain a product of sufficiently high quality. By yield it is meant herein percent yield, which is well-known as determined according to the following equation:

% yield=(actual yield)/(theoretical yield)×100

As is well-known, the actual yield and theoretical yield may be based on weight percent or mole percent. The actual % yield is a dimensionless number.

As discussed in International Publication No. WO 2012/091968, certain Lewis acids that may essentially require no activation time have been evaluated as polymerization catalysts. However, some Lewis acids may become deactivated rapidly and may not be capable of producing high molecular weight polymers or of obtaining high conversions of alkylene oxides to polymer. Further, high amounts of alkaline catalysts, such as sodium hydroxide may require treatment such as filtration and/or acid finishing/neutralization (e.g., as discussed in U.S. Pat. No. 5,468,839) to reduce the base content of the resultant product. The use of a sufficiently low amount of Lewis acid catalysts and optionally a DMC catalyst may eliminate the need for such treatment, while also providing for control and/or selectivity. However, certain Lewis acids may promote undesirable side reactions. The presence of certain side products in a polyol product may necessitate performing an additional finishing step on the resultant product.

Embodiments relate to certain Lewis acid catalysts, and processes using such Lewis acid catalysts, that may provide advantages with respect to minimizing side reactions such as those that produce undesired side-products and increasing yield of the desired products, while still allowing for precise control of the polymerization reaction. By Lewis acid it is meant a substance that can accept a pair of electrons. In other words, a Lewis acid in an electron-pair acceptor.

Embodiments may relate to providing polyol polymers having a desirable high yield, e.g., of EO capped polyether polyols and/or polyols prepared using a mixed feed of EO and another alkylene oxide. By EO capped polyols it is meant polyether polyols chains that have the addition of ethylene oxide (e.g., ethylene oxide only and essentially excluding intended addition of any other alkylene oxides such as propylene oxide and butylene oxide) on at least one end of such chain. EO capping may be performed on a polyether polyol (e.g., derived from propylene oxide, ethylene oxide, and/or butylene oxide). EO capping may result in a polyol having a high primary hydroxyl content (e.g., at least 30%, at least 40%, at least 50%, at least 60%, at least 70%, at least 80%, etc.) For a mixed feed process, copolymerization of EO and another alkylene oxide such as propylene oxide and/or butylene oxide may be performed on a starter compound and may result in a polyol having a higher primary hydroxyl content than that prepared with a feed of propylene oxide alone.

During the polymerization process to form a polyether polyol, some Lewis acid catalysts such as the tris(pentafluorophenyl)borane catalyst, may have a disadvantage in that certain side reactions may occur at undesirable levels (depending on the outcome desired). An example of such side reactions is the tris(pentafluorophenyl)borane catalyst-assisted formation of acetaldehyde as shown below in Schematic 1, which may occur in the presence of alcohols and may lead to the lack of desired chemoselectivity for the resultant polyether polyol. Further, high amount of formation of acetaldehyde or other volatile side-products may result in poor yield.

Further, a subsequent acetaldehyde-alcohol coupling reaction to form an acetal linkage, may result in higher molecular weight species as compared to when the coupling is not present and/or may make molecular weight control challenging especially at a commercial scale. Also, the water by-product that results from the coupling reaction could potentially consume monomer and result in the formation of diols and/or alter the catalytic activity of the tris(pentafluorophenyl)borane catalyst. Further, when the resultant product is used to form a polyurethane polymer, acetal linkages may be found at undesirable levels, which could potentially degrade over the life of the polyurethane polymer based product depending on the application.

Accordingly, in exemplary embodiments, a reaction system for forming a polyether polyol (such as an ethylene oxide based polyol) uses a Lewis acid catalyst (e.g., in a low amount such that filtration and acid finishing/neutralization are not required for the resultant polyether polyol) that minimizes side reactions and optionally may be combined with a DMC catalyst. For example, it is proposed to use arylborane catalysts that have at least one fluoroalkyl-substituted phenyl group, which may allow for improvements with respect to selectively minimizing side reactions so as to improve yield of desired EO based products and/or for precise control of the polymerization reaction (such as an EO-capping reaction).

In particular, it has been found that arylborane catalysts containing at least one fluoroalkyl substituents may significantly decrease the side-reactions leading to lower acetal linkages in the backbone. It is believed that the fluoroalkyl groups may impart unique properties to the metal (such as boron) active center. For example, the Hammett constant (σ) for a fluorine group in the para position σ_(p)=0.06 whereas that for a CF₃ group in the para position is 0.54. As such, a CF₃ group may act as a unique electron withdrawing group, which is in part related to the inability of F atoms to donate into the ring.

Embodiments, relate to forming a polyether polyol (e.g., an ethylene oxide based polyol) with a high yield. The polyether polyol may have a relatively high number average molecular weight (i.e., greater than 500 g/mol, greater than 1000 g/mol, greater than 2,500 g/mol such as from 2,600 g/mol to 12,000 g/mol, 3,000 g/mol to 6,000 g/mol, etc.) The polyether polyol may have a specified primary hydroxyl group content (e.g., from 30% to 95%, based on a total number of hydroxyl groups). For example, the Lewis acid catalyst may be used to enable a desired amount of ethylene oxide capping for the resultant polyether polyol as a means toward achieving a desired primary hydroxyl group content. Certain primary hydroxyl content values may be sought after for specific end use applications of polyurethanes, based on a desired reactivity speed. For example, some end use applications may seek a rapid reactivity speed, for which a relatively higher primary hydroxyl group content may be sought. Other end use applications may seek a relatively slow reactivity speed, for which a lower primary hydroxyl group content may be sought.

According to exemplary embodiments, a catalyst component for forming the polyether polyol may utilize the Lewis acid catalyst and optionally the DMC catalyst. For example, the Lewis acid catalyst may be used without the DMC catalyst, or the DMC catalyst and the Lewis acid catalyst may be used simultaneously or sequentially added. For example, in a DMC-Lewis acid dual catalyst system, a polymerization method may include initially adding a DMC catalyst and later adding the Lewis acid catalyst that is separately provided and allowed to react at a lower temperature than the temperature at which the DMC catalyst was added. The Lewis acid catalyst may be active at a lower temperature range (e.g., from 60° C. to 115° C.) than a temperature range at which the DMC catalyst may be active (e.g., from 125° C. to 160° C.).

Polyether polyols include polyols that have multiple ether bonds. Exemplary polyether polyols include polyether hybrid polyols (such as polyether carbonate polyols and polyether ester polyols). The polyether polyols are produced by polymerizing an alkylene oxide component that includes at least one alkylene oxide and an initiator component that includes at least one initiator compound. The initiator compound has one or more functional groups at which the alkylene oxide can react to begin forming the polymer chains. The main functions of the initiator compound are to provide molecular weight control and to establish the number of hydroxyl groups that the monol or polyol product will have. The polyether carbonate may be produced by polymerizing carbon dioxide, at least one alkylene oxide, and an initiator compound. The polyether ester may be produced by polymerizing at least one alkylene oxide with a carboxylic acid initiator.

Lewis Acid Catalyst

According to exemplary embodiments, the Lewis acid catalyst has the general formula M(R¹)₁(R²)₁(R³)₁(R⁴)_(0 or 1), whereas M is boron, aluminum, indium, bismuth or erbium, R¹ includes a first fluoroalkyl-substituted phenyl group, R² includes a second fluoroalkyl-substituted phenyl group or a first fluoro substituted phenyl group or a chloro-substituted phenyl group (i.e., first fluoro/chloro-substituted phenyl group), R³ includes a third fluoroalkyl-substituted phenyl group or a second fluoro-substituted phenyl group or a chloro-substituted phenyl group (i.e., second fluoro/chloro-substituted phenyl group), and optional R⁴ is a functional group or functional polymer group. The M in the general formula may exist as a metal salt ion or as an integrally bonded part of the formula. R¹, R², R³ and R⁴ are each independent of each other, e.g., a fluoroalkyl-substituted phenyl group of R¹ may be the same as or different from a fluoroalkyl-substituted phenyl group of R². Though, R¹ is different from at least one of R² and R³, such that each of R¹, R², and R³ are not all the same (e.g., same fluoroalkyl-substituted phenyl group), but R¹ may or may not be the same as R² or R³.

R¹ may include the first fluoroalkyl-substituted phenyl group or may consist essentially of the first fluoroalkyl-substituted phenyl group. Similarly, R² may include the second fluoroalkyl-substituted phenyl group or the first fluoro/chloro-substituted phenyl group, or consist essentially of the second fluoroalkyl-substituted phenyl group or the first fluoro/chloro-substituted phenyl group. Similarly, R³ may include the third fluoroalkyl-substituted phenyl group or the second fluoro/chloro-substituted phenyl group, or consist essentially of the third fluoroalkyl-substituted phenyl group or the second fluoro/chloro-substituted phenyl group. Similarly, R⁴ may include the functional group or functional polymer group, or consist essentially of the R⁴ is the functional group or functional polymer group.

With respect to R¹, R², and R³, by fluoroalkyl-substituted phenyl group it is meant a phenyl group that includes at least one hydrogen atom replaced with a fluoroalkyl group, which is an alkyl group with at least one hydrogen atom replaced with a fluorine atom. For example, the fluoroalkyl group may have the structure C_(n)H_(m)F_(2n+1−m), whereas n is greater than or equal to 1 and less than or equal to 5. Also, m is a number that reflects a balance of the electrical charges to provide an overall electrostatically neutral compound, e.g., can be zero, one or greater than one. The phenyl group of the fluoroalkyl-substituted phenyl may be substituted to include other groups in addition to the at least one fluoroalkyl group, e.g., a fluorine atom and/or chlorine atom that replaces at least one hydrogen of the phenyl group. For example, R¹, R², or R³ may be a fluoro/chloro-fluoroalkyl-substituted phenyl group (meaning one fluoro or chloro group and at least one fluoroalkyl group are substituted on the phenyl group), difluoro/chloro-fluoroalkyl-substituted phenyl group (meaning two fluoro, two chloro, or a fluoro and chloro group and at least one fluoroalkyl group are substituted on the phenyl group), trifluoro/chloro-fluoroalkyl-substituted phenyl group (meaning three fluoro, three chloro, or a combination of fluoro and chloro groups totaling three and at least one fluoroalkyl group are substituted on the phenyl group), or tetrafluoro/chloro-fluoroalkyl-substituted phenyl group (meaning four fluoro, four chloro, or a combination of fluoro and chloro groups totaling four and one fluoroalkyl group are substituted on the phenyl group).

With respect to R² and R³, by fluoro-substituted phenyl group it is meant a phenyl group that includes at least one hydrogen atom replaced with a fluorine atom. By chloro-substituted phenyl group it is meant a phenyl group that includes at least one hydrogen atom replaced with a chlorine atom. The phenyl group of the fluoro/chloro-substituted phenyl group may be substituted with other groups (such as may include a combination of fluoro, chloro, and/or hydrogens), but excludes any fluoroalkyl groups (e.g., excludes the group having the structure C_(n)H_(m)F_(2n+1−m) discussed above). Accordingly, the fluoro/chloro-substituted phenyl group is differentiated from the fluoroalkyl-substituted phenyl group, by the exclusion of any fluoroalkyl groups substituted on the phenyl ring.

With respect to optional R⁴, the functional group or functional polymer group may be a Lewis base that forms a complex with the Lewis acid catalyst (e.g., a boron based Lewis acid catalyst) and/or a molecule or moiety that contains at least one electron pair that is available to form a dative bond with a Lewis acid. The Lewis base may be a polymeric Lewis base. By functional group or functional polymer group it is meant a molecule that contains at least one of the following: water, an alcohol, an alkoxy (examples include a linear or branched ether and a cyclic ether), a ketone, an ester, an organosiloxane, an amine, a phosphine, an oxime, and substituted analogs thereof. Each of the alcohol, linear or branched ether, cyclic ether, ketone, ester, alkoxy, organosiloxane, and oxime may include from 2-20 carbon atoms, from 2-12 carbon atoms, from 2-8 carbon atoms, and/or from 3-6 carbon atoms.

For example, the functional group or functional polymer group may have the formula (OYH)n, whereas O is O oxygen, H is hydrogen, Y is H or an alkyl group, and n is an integer (e.g., an integer from 1 to 100). However, other known functional polymer groups combinable with a Lewis acid catalyst such as a boron based Lewis acid catalyst may be used. Exemplary cyclic ethers include tetrahydrofuran and tetrahydropyran. Polymeric Lewis bases are moieties containing two or more Lewis base functional groups such as polyols and polyethers based on polymers of ethylene oxide, propylene oxide, and butylene oxide. Exemplary polymeric Lewis bases include ethylene glycol, ethylene glycol methyl ether, ethylene glycol dimethyl ether, diethylene glycol, diethylene glycol dimethyl ether, triethylene glycol, triethylene glycol dimethyl ether, polyethylene glycol, polypropylene glycol, and polybutylene glycol.

According to exemplary embodiments, the Lewis acid catalysts may have the following structure that includes at least one fluoroalkyl (Y) group substituted on a phenyl group, whereas that are at least two different substituted groups (i.e., Ar¹ and Ar²) and optionally at least one fluoro or chloro (X) substituted on another phenyl group:

Further, the Lewis acid catalysts may have the following structures:

Further, the Lewis acid catalysts may have the following structures:

Whereas for exemplary structures, Ar¹ is chosen from the following, referred to as the Set 1 structures:

Whereas for exemplary structures, Are is chosen from the following, referred to as Set 2 structures:

According to exemplary embodiments, the Lewis acid catalyst is a boron based Lewis acid catalyst that has the general formula B(R¹)₁(R²)₁(R³)₁(R⁴)_(0 or 1), whereas R¹ is the first fluoroalkyl-substituted phenyl group (e.g., any structure from Set 1 structures), R² is the second fluoroalkyl-substituted phenyl group (e.g., any structure from Set 1 structures) or the first fluoro/chloro-substituted phenyl group (e.g., any structure from Set 2 structures), R³ is the third fluoroalkyl-substituted phenyl group (e.g., any structure from Set 1 structures) or the second fluoro/chloro-substituted phenyl group (e.g., any structure from Set 2 structures), and optional R⁴ is the functional group or functional polymer group. In exemplary embodiments, at least one of R¹ or R² or R³ is a 3,4- or 3,5-bis(fluoroalkyl)-substituted phenyl group (e.g., a 3,4 or 3,5-bis(trifluoromethyl)-substituted phenyl group). For example, R⁴ is a cyclic ether having 3-10 carbon atoms.

Exemplary structures for the Lewis acid catalysts, where M is Boron are shown below:

Basic Catalyst Structure Ar¹ = R¹, R², or R³ Ar² = R¹, R², or R³ Ar³ = R¹, R², or R³ B = Boron Any of the structures may include optional R = R⁴      

Exemplary Structure 1

Exemplary Structure 2

Exemplary Structure 3

Exemplary Structure 4

Exemplary Structure 5

Exemplary Structure 6

Exemplary Structure 7

Exemplary Structure 8

Exemplary Structure 9

Exemplary Structure 10

Exemplary Structure 11

Exemplary Structure 12

Exemplary Structure 13

While the above illustrates exemplary structures that include boron, similar structures may be used that include other metals such as aluminum, indium, bismuth, and/or erbium. Further, exemplary embodiments may utilize a blend of catalyst, e.g., using one or more of the catalysts structures above.

Without intending to be bound by this theory, certain R⁴ may help improve shelf life of the catalyst, e.g., without significantly compromising catalyst activity when utilized in a polymerization reaction. For example, the catalyst comprising M, R¹, R², and R³ may be present in the form with the optional R⁴ (form M(R¹))₁(R²)₁(R³)₁(R⁴)₁) or without the optional R⁴ (form M(R¹)₁(R²)₁(R³)₁). The optional R⁴ may dissociate step-wise from M(R¹)₁(R²)₁(R³)₁(R⁴)₁ to give free M(R¹)₁(R²)₁(R³)₁, as shown below for M=B, which free M(R¹)₁(R²)₁(R³)₁ may be a catalyst for an alkoxylation/polymerization process, and/or may dissociate from M(R¹)₁(R²)₁(R³)₁(R⁴)₁ in a concerted or other single-step process with the alkylene oxide to give a catalyst for an alkoxylation/polymerization process.

For example, the catalyst including M, R¹, R², and R³ may be present in the form with and without the optional R⁴ group, as shown below.

The ability of the optional R⁴ group to protect the boron, aluminum, indium, bismuth and erbium center from inadvertent decomposition reactions may be related to the decrease in the accessible volume of the center. The accessible volume of the center is defined as the volume around the atom, such as boron atom, that is available for interaction with a small molecule like a solvent.

Accessible volume of Catalyst boron (%)

27

10

Suitable R⁴ groups that can help increase catalyst shelf stability, e.g., without compromising catalyst activity, include diethyl ether, cyclopentyl methyl ether, methyl tertiary-butyl ether, tetrahydrofuran, tetrahydropyran, 1,4-dioxane, acetone, methyl isopropyl ketone, isopropyl acetate, and isobutyl acetate.

The Lewis acid catalyst used in exemplary embodiments may be a blend catalyst that includes one or more Lewis acid catalyst (e.g., each having the general formula B(R¹)₁(R²)₁(R³)₁(R⁴)_(0 or 1)) and optionally at least one other catalyst (such as catalyst known the art for producing polyether polyols). The blend catalyst may optionally include other catalysts, in which Lewis acid catalysts having the general formula account for at least 25 wt %, at least 50 wt %, at least 70 wt %, at least 75 wt %, at least 80 wt %, at least 85 wt %, at least 90 wt %, at least 95 wt %, at least 99 wt %, etc., of the total weight of the blend catalyst.

DMC Catalyst

The catalyst component may optionally include DMC catalysts. Exemplary DMC catalysts and method of producing DMC catalyst are described, e.g., in U.S. Pat. Nos. 3,278,457, 3,278,458, 3,278,459, 3,404,109, 3,427,256, 3,427,334, 3,427,335, and 5,470,813. An exemplary type of DMC catalyst is a zinc hexacyanocobaltate catalyst complex. The mDMC catalyst complexes may be prepared using modified methods of forming the DMC catalysts. The DMC catalyst, e.g., ones that are known in the art, may be used in the catalyst system that includes the Lewis acid catalyst. The DMC catalyst may be the first or second catalyst that is provided.

For example, the DMC catalysts may be represented by the Formula 1:

M_(b)[M¹(CN)_(r)(X)_(t)]_(c)[M²(X)₆]_(d) .nM³ _(x)A_(y)   (Formula 1)

wherein M and M³ are each metals; M¹ is a transition metal different from M. X¹ represents a group other than cyanide that coordinates with the M¹ ion. M² is a transition metal. X² represents a group other than cyanide that coordinates with the M² ion. X¹ or X² may each independently be a halogen, sulfate, nitrate, phosphate, carbonate, or chlorate. In exemplary embodiments, X¹ and X² are the same and are chloride. A¹ represents an anion; b, c and d are numbers that reflect an electrostatically neutral complex; r is from 4 to 6; t is from 0 to 2; x and y are integers that balance the charges in the metal salt M³ _(x)A_(y), and n is zero or a positive integer. For example, n is from 0.01 to 20. The foregoing formula does not reflect the presence of neutral complexing agents such as t-butanol which are often present in the DMC catalyst complex.

Referring to Formula (I), M and M³ each are a metal ion independently selected from (e.g., from the group consisting of): Zn²⁺, Fe²⁺, Co⁺²⁺, Ni²⁺, Mo⁴⁺, Mo⁶⁺, Al⁺³⁺, V⁴⁺, V⁵⁺, Sr²⁺, W⁴⁺, W⁶⁺, Mn²⁺, Sn²⁺, Sn⁴⁺, Pb²⁺, Cu²⁺, La³⁺ and Cr³⁺. Exemplary embodiments include at least Zn²⁺. Further, M¹ and M² each are a metal ion independently selected from (e.g., from the group consisting of): Fe³⁺, Fe²⁺, Co³⁺, Co²⁺, Cr²⁺, Cr³⁺, Mn²⁺, Mn³⁺, Ir³⁺, Ni²⁺, Rh³⁺, Ru²⁺, V⁴⁺, V⁵⁺, Ni²⁺, Pd²⁺, and Pt³⁺. Among the foregoing, those in the plus-three oxidation state may be used for the M′ and M² metal. Exemplary embodiments include Co⁺³ and/or Fe⁺³.

Suitable anions A include, but are not limited to, halides such as chloride, bromide and iodide, nitrate, sulfate, carbonate, cyanide, oxalate, thiocyanate, isocyanate, perchlorate, isothiocyanate, an alkanesulfonate such as methanesulfonate, an arylenesulfonate such as p-toluenesulfonate, trifluoromethanesulfonate (triflate), and a C₁₋₄ carboxylate. Exemplary embodiments include the chloride ion.

Referring to Formula (I), r is an integer that is 4, 5 or 6. In exemplary embodiments, r is 4 or 6. Further, t is an integer from 0 to 2, and in exemplary embodiments t is 0. The sum of r+t may equal six.

In exemplary embodiments, the DMC catalyst is a zinc hexacyanocobaltate catalyst complex. The DMC catalyst may be complexed with t-butanol. The DMC catalyst used in exemplary embodiments may be a blend catalyst that includes of one or more DMC catalysts. The blend catalyst may optionally include a non-DMC catalyst, in which the DMC catalysts account for at least 75 wt % of the total weight of the blend catalyst. The blend catalyst may exclude any of Lewis acid catalyst that is added at a later time in the dual catalyst system.

Monomers

The monomers used to provide the polyether polyol include at least one ethylene oxide. The monomers may additionally include other monomers, such as propylene oxide (1,2-propylene oxide), butylene oxide (1,2-butene oxide), the alkylene oxide monomers having at least three carbon atoms are selected from 1,2-alkene oxide monomers having from three to ten carbon atoms (linear or branched) and/or arylalkylene oxide monomers. Exemplary other monomers include pentylene oxide (also known as 1,2-epoxypentane), hexylene oxide (also known as 1,2-epoxyhexane), octylene oxide (also known as 1,2-epoxyoctane), nonylene oxide (also known as 1,2-epoxynonane), decylene oxide (also known as 1,2-epoxydecane), isobutylene oxide, 4-methyl-1-pentylene oxide, and styrene oxide.

Use of the Catalyst Component

In embodiments where the Lewis acid catalyst is used the alkoxylation of low hydroxyl equivalent weight starter compounds, also referred to as initiators, may proceed directly from the starter compound to a finished polyether polyol by the polymerization of one or more alkylene oxides. Further, the use of the Lewis acid catalyst during the polymerization reaction may reduce certain side reactions that lead to increased polydispersity and/or to increased acetal content in a final product.

The starter compound, also referred to as an initiator, has a low molecular weight and a nominal hydroxyl functionality of at least 2. The initiator is any organic compound that is to be alkoxylated in the polymerization reaction. The initiator may contain as many as 12 or more hydroxyl groups. For example, the initiator may be a diol, triol or hexol. Mixtures of starter compounds/initiators may be used. The initiator will have a hydroxyl equivalent weight less than that of the polyether product, e.g., may have a hydroxyl equivalent weight of less than 3500 g/mol equivalence, less than 333 g/mol equivalence, less than 300 g/mol equivalence, greater than 30 g/mol equivalence, from 30 to 300 g/mol equivalence, from 30 to 250 g/mol equivalence, from 50 to 250 g/mol equivalence, etc. Exemplary, initiator compounds include, but are not limited to, ethylene glycol, diethylene glycol, triethylene glycol, propylene glycol, dipropylene glycol, tripropylene glycol, 1,4-butanediol, 1,6-hexanediol, 1,8-octanediol, cyclohexane dimethanol, glycerin, trimethylolpropane, trimethylolethane, pentaerythritol, sorbitol, sucrose, and/or alkoxylates (especially ethoxylates and/or propoxylates) any of these that have a number average molecular weight less than that of the product of the polymerization (e.g., less than 5000 g/mol, less than 4000 g/mol, less than 3000 g/mol, less than 2000 g/mol, and/or less than 1000 g/mol).

The starter compound/initiator may be a low molecular weight polyether polyol that has been formed using an alkylene oxide such as propylene oxide, ethylene oxide, and/or butylene oxide (e.g., which is polymerized with another starter compound/initiator). The starter compound may be a diol or triol. For example, the starter compound is an all-propylene oxide-based diol or triol. The starter compound may have a hydroxyl functional based equivalent weight of may have a hydroxyl equivalent weight of less than 3500 g/mol equivalence, less than 333 g/mol equivalence, less than 300 g/mol equivalence, greater than 30 g/mol equivalence, from 30 to 300 g/mol equivalence, from 30 to 250 g/mol equivalence, from 50 to 250 g/mol equivalence, etc.

When the Lewis acid catalyst is used, the temperature of the reactor may be reduced at least 20° C. as compared to when the DMC catalyst is used. For example, the temperature for use of a DMC catalyst may be from 125° C. to 160° C. (e.g., during a time at which an ethylene oxide feed is gradually/slowly added to the reactor and after the time at which the starter compound is mixed with the DMC catalyst). The temperature for use of the Lewis acid catalyst may be from 25° C. to 115° C. and/or from 60° C. to 115° C. In exemplary embodiments, the control of the relative contribution of a mixture containing an active DMC catalyst and an active Lewis acid may enable the Lewis acid to dominate the addition of alkylene oxide onto chain ends.

In an exemplary embodiment, when the polyether polyol is derived from propylene oxide based initiator (e.g., a polyoxypropylene starter compound), during the polymerization process ethylene oxide may be added to the reaction mixture to form the polyether polyol having a number average molecular weight of greater than the number average molecular weight of the initiator. For example, the polyether polyol may have a molecular weight of at least 250 g/mol, at least 1000 g/mol, at least 2000 g/mol, at least 3000 g/mol, at least 5000 g/mol, at least 6000 g/mol, and/or at least greater than 100 g/mol.

The polymerization reaction can be performed in any type of vessel that is suitable for the pressures and temperatures encountered. In a continuous or semi-continuous process the vessel may have one or more inlets through which the alkylene oxide and additional initiator compound may be introduced during the reaction. In a continuous process, the reactor vessel should contain at least one outlet through which a portion of the partially polymerized reaction mixture may be withdrawn. A tubular reactor that has single or multiple points for injecting the starting materials, a loop reactor, and a continuous stirred tank reactor (CSTR) are all suitable types of vessels for continuous or semi-continuous operations. An exemplary process is discussed in U.S. Patent Publication No. 2011/0105802.

The resultant polyether polyol product may be further treated, e.g., in a flashing process and/or stripping process. For example, the polyether polyol may be treated to reduce catalyst residues even though the catalyst residue may be retained in the product. Moisture may be removed by stripping the polyol. The polyether polyol derived from ethylene oxide, according to embodiments, may have a Lewis acid catalyst concentration (in ppm in the final polyol) of from 50 ppm to 1000 ppm (e.g., 100 ppm to 500 ppm and/or 100 ppm to 250 ppm).

The polymerization reaction may be characterized by the “build ratio”, which is defined as the ratio of the number average molecular weight of the polyether product to that of the initiator compound. This build ratio may be as high as 160, but is more commonly in the range of from 2.5 to about 65 and still more commonly in the range of from 2.5 to about 50. The build ratio is typically in the range of from about 2.5 to about 15, or from about 7 to about 11 when the polyether product has a hydroxyl equivalent weight of from 85 to 400.

Exemplary embodiments relate to preparing the polyether polyols using one or more of certain Lewis acid catalysts as polymerization catalysts that may achieve a lower acetal content in the resultant polyether polyols (e.g., less than 5.0 mol %, less than 4.0 mol %, less than 3.0 mol %, less than 1.5 mol %, less than 1.0 mol %, less than 0.8 mol %, less than 0.5 mol %, less etc.), based on the total moles of carbon in the resultant polyol chains, while still receiving high molecular weight polyols (e.g., poly-ethylene oxide polyols, poly-propylene oxide/ethylene oxide polyols, poly-ethylene oxide/butylene oxide polyols, etc.)

Exemplary embodiments related to preparing EO-capped polyether polyols at a high yield, e.g., a yield of at least 50 wt %, at least 60 wt %, at least 70 wt %, at least 80 wt %, at least 90 wt %, at least 95 wt %, etc., based on a total weight of the resultant polyol product.

Exemplary embodiments relate to using one or more of certain Lewis acid catalyst as polymerization catalyst, such that use of the Lewis acid catalyst may result in higher activation barriers to aldehyde formation, which is an undesired product, as compared to the activation barrier for forming the desired polyether polyol product or intermediate. As such the formation of the desired product or intermediate product may be favored during the polymerization process compared to the undesired products. For example, the activation barrier to aldehyde formation may be greater than 3.5 kcal/mol, greater than 5.0 kcal/mol, greater than 6.0 kcal/mol, and/or greater than 8.0 kcal/mol. The activation barrier to aldehyde formation may be less than 30 kcal/mol and/or less than 20 kcal/mol.

Polyether polyols produced in accordance with embodiments may be useful for making polyurethanes. The polyurethane polymers may be prepared as the reaction product of the polyether polyol and an isocyanate (such as a polyisocyanate, of which examples include methylenediphenyl diisocyanate also known as MDI and toluene diisocyanate also known as TDI). For example, higher equivalent weight polyether polyol products may be useful in making elastomeric or semi-elastomeric polyurethane products, including noncellular or microcellular elastomers, coatings, adhesives, sealants, composites, and flexible, rigid, and viscoelastic polyurethane foams. The polyurethane foams may be made in a slabstock or molding process.

All parts and percentages are by weight unless otherwise indicated. All molecular weight values are based on number average molecular weight unless otherwise indicated.

EXAMPLES

Approximate properties, characters, parameters, etc., are provided below with respect to various working examples, comparative examples, and the materials used in the working and comparative examples.

Catalyst Synthesis

The general production for catalyst synthesis is as follows. Unless otherwise noted, all experimental procedures and manipulations of chemical substances are performed in a nitrogen-purged glove box or on a Schlenk line. All bulk reaction solvents (toluene, diethyl ether, hexane, tetrahydrofuran (THF)) are dried by passage through columns of alumina and Q5 reactive scavenger. All other solvents are purchased from Aldrich anhydrous grade and stored over activated 3 Å molecular sieves prior to use. NMR solvents (CDCl₃ and C₆D₆), obtained from Cambridge Isotope Laboratories, Inc., are dried over molecular sieves or, in the case of C₆D₆, dried using Na/K alloy. Further, 1-bromo-2,3,4,5,6-pentafluorobenzene,1-bromo-3,5-bis(trifluoromethyl)benzene, 1-bromo-3,4,5-trifluorobenzene, 1-bromo-2,6-difluorobenzene, 1-bromo-2-chloro-4,6-difluorobenzene, 1-bromo-2,4,6-trifluorobenzene, 1-bromo-2-fluoro-3-trifluoromethylbenzene, 1-bromo-2-fluoro-4-trifluoromethylbenzene, 1-bromo-2,5-bis(trifluoromethyl)benzene, and 1-bromo-2,4-difluoro-3-trifluoromethylbenzene are purchased from Oakwood Chemical and used as received. 1-Bromo-2,3,5,6-tetrafluoro-4-trifluoromethylbenzene is purchased from Alfa Aesar and used as received. Also, n-butyllithium (nominal 1.6 or 2.5 M solution in hexane), triisopropylborate, boron trichloride (1.0 M solution in toluene), chlorotrimethylsilane, hexachlorobenzene, and anhydrous HCl (2.0 M solution in diethyl ether) are obtained from Sigma-Aldrich and used as received. Further, n-butyllithium (1.6 or 2.5 M solution in hexane) is titrated before use using 1.00 M decanol in toluene with 1,10-phenanthroline as an indicator. Bis(3,5-bis(trifluoromethyl)phenyl)chloroborane (Samigullin et al., Organometallics, 2014, 33, 3564-3569) is prepared according to literature procedures.

Multinuclear NMR spectra (¹H, ¹¹B, ¹³C, ¹⁹F) are collected on one of the following instruments: Varian MR-400 or Varian VNMRS-500. The ¹H and ¹³C NMR chemical shifts are referenced in parts per million relative to residual solvent peaks: ¹H—7.15 ppm for C₆D₆, 7.25 ppm for CDCl₃; ¹³C—128.00 ppm for C₆D₆, and 77.00 ppm for CDCl₃. Boron-11 NMR chemical shifts are referenced externally to BF₃(Et₂O) (0 ppm), and ¹⁹F NMR chemical shifts are referenced externally to CFCl₃ (0 ppm). Sub-ambient reaction temperatures, except when dry ice or ice were the sole means of cooling, are measured using an Extech Instruments EasyView™10 Dual K model EA 10 thermometer with a fine JKEM sensor PTFE wire K 36INJ.

Starting materials for the catalyst are prepared as follows:

Starting material, (3,5-bis(trifluoromethyl)phenyl)diisopropoxyborane, is prepared according to Schematic 2:

In particular, in a first stage, n-butyllithium (23.0 mL, 2.61 M in hexanes, 60.0 mmol) is added with stirring to a cold (−78° C., CO₂(s) bath) solution of 1-bromo-3,5-bis(trifluoromethyl)benzene (18.5 g, 63.2 mmol) in diethyl ether (200 mL). The reaction mixture is stirred for 3 hours at −78° C., during which time precipitate is formed. Triisopropylborate (11.9 g, 63.1 mmol) in ether (20 mL) is added slowly to the reaction mixture. The reaction mixture is stirred for 1 hour at −78° C., and then is allowed to warm to ambient temperature. The reaction mixture is further stirred for 1 hour to give a slightly cloudy solution. The reaction mixture is filtered and the volatiles are removed under reduced pressure to give a solid. The solid is triturated with hexane, filtered, and the volatiles are again removed under reduced pressure to give lithium(diethyletherate) (3,5-bis(trifluoromethyl)phenyl)triisopropoxyborate as a colorless powder. Yield: 23.2 g (95%).

In a second stage, hydrogen chloride solution (12.3 mL, 2 M in ether, 24.6 mmol) is added at ambient temperature to a solution of lithium(diethyletherate) (3,5-bis(trifluoromethyl)phenyl)triisopropoxyborate (prepared in first stage, 8.00 g, 19.6 mmol) in diethyl ether (100 mL). Precipitate may form immediately upon addition. The reaction mixture is stirred for two hours, and then filtered. The volatiles are removed under reduced pressure. The resultant residue is extracted with hexane, filtered, and the volatiles are again removed under reduced pressure to give the (3,5-bis(trifluoromethyl)phenyl)diisopropoxyborane as an oil. Yield: 5.10 g (76%).

Starting material, bis(3,5-bis(trifluoromethyl)phenyl)isopropoxyborane, is prepared according to Schematic 3:

In particular, in a first stage, n-butyllithium (5.3 mL, 2.6 M in hexanes, 60 mmol) is added with stirring to a cold (−78° C., CO₂(s) bath) solution of 1-bromo-3,5-bis(trifluoromethyl)benzene (4.26 g, 14.5 mmol) in diethyl ether (200 mL). The reaction mixture is stirred for 1 hour at −78° C.; precipitate forms during this time. (3,5-Bis(trifluoromethyl)phenyl)diisopropoxyborane (4.82 g, 14.1 mmol) in ether (15 mL) is added slowly to the cold reaction mixture. The reaction mixture is stirred for 1 hour at −78° C. (precipitate still present) and then allowed to warm to ambient temperature. The reaction mixture is stirred overnight to give a clear solution. The volatiles are removed under reduced pressure to give a crystalline-appearing solid. The solid is dissolved in hexane, and the resultant solution is filtered and placed in the freezer (−33° C.) over the weekend. A large amount of crystalline material is formed during this time. The supernatant is decanted and the volatiles are removed under reduced pressure to give a colorless crystalline material. Yield of lithium(diethyletherate) bis(3,5-bis(trifluoromethylphenyl)diisopropoxyborate: 8.23 g, (94%).

In a second stage, hydrogen chloride solution (5.5 mL, 2 M in ether, 11 mmol) is added at ambient temperature to a solution of lithium(diethyletherate) bis(3,5-bis(trifluoromethyl)phenyl)diisopropoxyborate (prepared in first stage, 5.00 g, 7.86 mmol) in diethyl ether (100 mL). Precipitate may form immediately upon addition. The reaction mixture is stirred for one hour and the volatiles are removed under reduced pressure. The resultant residue is extracted with hexane, filtered, and the volatiles are again removed under reduced pressure to give bis(3,5-bis(trifluoromethyl)phenyl)isopropoxyborane as a colorless powder. Yield: 3.98 g, (102%; product contains residual solvent).

Starting material, (2,3,4,5,6-pentafluorophenyl)(3,5-bis(trifluoromethyl)phenyl)-(isopropoxy)borane, is prepared according to Schematic 4:

In particular, in a first stage, n-butyllithium (6.0 mL, 2.6 M in hexanes, 16 mmol) is added with stirring to a cold (between −95° C. and −93° C., CO₂(s), then N₂(l), methanol bath) solution of 1-bromo-2,3,4,5,6-pentafluorobenzene (4.47 g, 16.5 mmol) in diethyl ether (200 mL). The reaction mixture is stirred for 1 hour at −90° C.; a small amount of precipitate is formed during this time. (3,5-Bis(trifluoromethyl)phenyediisoproxyborane (5.00 g, 14.6 mmol) in ether (15 mL) is added slowly. The reaction mixture is stirred for 2 hours at −90° C. and then allowed to warm to −78° C. and stir for 2-3 more hours. The reaction mixture is allowed to warm to ambient temperature and is stirred overnight to give a clear solution. The volatiles are removed under reduced pressure to give a brownish yellow oil. The oily residue is extracted with hexane and filtered. The volatiles are removed from the hexane solution under reduced pressure to give a brownish yellow oil. Hexane (50 mL) is added to dissolve the oil. THF (5 mL) is added to the solution and the volatiles are removed under reduced pressure to give a solid. The solid is dissolved in hexane and the solution is placed in the freezer (−33° C.) overnight; solid crystalline material forms during this time. The supernatant is drained from the crystalline material and the material is washed with hexane. After drying under vacuum, lithium bis(tetrahydrofuranate) (2,3,4,5,6-pentafluorophenyl)(3,5-bis(trifluoromethyl)phenyl)diisopropoxyborate is isolated as an off-white brownish microcrystalline solid. Yield: 5.24 g (61%).

In a second stage, hydrogen chloride solution (6.0 mL, 2 M in ether, 12 mmol) is added at ambient temperature to a solution of lithium bis(tetrahydrofuranate) (2,3,4,5,6-pentafluorophenyl)(3,5-bis(trifluoromethyl)phenyl)diisopropoxyborate (prepared in first stage, 5.11 g, 7.73 mmol) in diethyl ether (75 mL). Precipitate may be formed immediately upon addition. The reaction mixture is stirred for about 30 minutes. The reaction mixture is then stirred overnight under very slightly reduced pressure in order to remove volatiles. A white solid is formed. The white solid is extracted with hexane, filtered, and the volatiles are removed to give (2,3,4,5,6-pentafluorophenyl)(3,5-bis(trifluoromethyl)phenyl)isopropoxyborane as a white solid. Yield: 3.46 g (100%).

Starting material, (3,5 -bis(trifluoromethyl)phenyl)(3,4,5-trifluorophenyl)isopropoxyborane, is prepared according to Schematic 5:

In particular, in a first stage, n-butyllithium (37.2 mL, 2.53 M in hexanes, 94.1 mmol) is added with stirring to a cold (−78° C., CO₂(s) bath) solution of 1-bromo-3,4,5-trifluorobenzene (27.6 g, 131 mmol) in diethyl ether (300 mL). The addition is done at a rate such that the temperature of the reaction mixture is maintained in a range between −73° C. to −70° C. The reaction mixture is stirred for 1 hour at −78° C. and formation of precipitate is noted. (3,5-Bis(trifluoromethyl)phenyl)diisopropoxyborane (32.2 g, 94.1 mmol) in ether (15 mL) is added slowly to the reaction mixture. The reaction mixture is allowed to warm to ambient temperature while stirring over the weekend to give a slightly cloudy solution. The solution is filtered and the volatiles are removed under reduced pressure to give a pasty crystalline-appearing solid, characterized by multinuclear NMR spectroscopy as lithium(diethyletherate) (3,5-bis(trifluoromethyl)phenyl)(3,4,5-trifluorophenyl)diisopropoxyborate. This solid is used in the next stage without any further purification.

In a second stage, the product from the first stage is dissolved in diethyl ether (150 mL) and hydrogen chloride solution (50 mL, 2 M in diethyl ether, 100 mmol) is added with formation of copious precipitate. The reaction mixture is allowed to stir over the weekend. The reaction mixture is filtered. The volatiles are removed from the filtrate under reduced pressure. The resultant residue is extracted with hexane, filtered, and the volatiles are removed under reduced pressure to yield a thick, light orange oil, characterized as (3,5-bis(trifluoromethyl)phenyl)(3,4,5-trifluorophenyl)isopropoxyborane. Yield: 32.6 g, (84%).

Starting material, (3,5-bis(trifluoromethyl)phenyl)(2,5-bis(trifluoromethyl)phenyl)isopropoxyborane, is prepared according to Schematic 6:

In particular, in a first stage, n-butyllithium (4.0 mL, 2.5 M in hexanes, 10 mmol) is added to a cold (between −101° C. and −99° C., CO₂(s), then N₂(l), methanol bath) solution of 1-bromo-2,5-bis(trifluoromethyl)benzene (3.00 g, 10.2 mmol) in diethyl ether (150 mL) with stirring. The reaction mixture is stirred for 2 hours at around −100° C. and then is allowed to warm up to −78° C. (3,5-Bis(trifluoromethyl)phenyl)diisopropoxyborane (3.51 g, 10.3 mmol) in ether (10 mL) is added slowly to the reaction mixture and the reaction mixture is allowed to warm to ambient temperature overnight while stirring . The volatiles are removed from the pale yellow, nearly clear, solution under reduced pressure to give a crystalline-appearing yellow solid. The yellow solid is dissolved in hexane, filtered, and concentrated under a nitrogen stream. Colorless crystals precipitate from the solution and these are isolated by filtration. NMR analysis of the crystals show pure desired compound. Yield of colorless crystals from the first crop: 3.32 g. The supernatant solution from the crystals is placed in the freezer overnight. Crystalline matter forms. The supernatant is pipetted out and discarded. The crystalline residue is dried under reduced pressure: 2.02 g. The total yield of the product, lithium(diethyletherate) (3,5-bis(trifluoromethyl)phenyl)(2,5-bis(trifluoromethyl)phenyl)diisopropoxyborate, is 5.34 g, (83%).

In a second stage, chlorotrimethylsilane (2.0 mL, 16 mmol) is added to a solution of lithium(diethyletherate) (3,5-bis(trifluoromethyl)phenyl)(2,5-bis(trifluoromethyl)phenyl)diisopropoxyborate (3.32 g, 5.21 mmol) in ether (10 mL) with rapid formation of precipitate. The reaction mixture is allowed to stir overnight. The reaction mixture is filtered and the volatiles are removed under reduced pressure. NMR analysis shows the reaction is complete. A second batch of lithium(diethyletherate) (3,5-bis(trifluoromethyl)phenyl)(2,5-bis(trifluoromethyl)phenyl)diisopropoxy borate (2.02 g, 3.18 mmol) is treated similarly with 2.0 mL of chlorotrimethylsilane and stirred for 3 hours. The second reaction mixture in this second stage is filtered and combined with the first reaction product. The volatiles are removed from the mixture under reduced pressure. The residue is extracted with hexane, filtered, and the volatiles are removed overnight at 40° C. under reduced pressure to give the product, (3,5-bis(trifluoromethyl)phenyl)(2,5-bis(trifluoromethyl)phenyl)isopropoxyborane, as a yellow oil, 3.47g, 83.4%.

The Catalyst samples are prepared as follows:

Catalyst 1 is the THF adduct of bis(3,5-bis(trifluoromethyl)phenyl)-(2,3,4,5,6-pentafluorophenyl)borane, which is prepared according to the following Schematic 7:

In particular, in a first stage, in an N₂-purged glove box, bis(3,5-bis(trifluoromethyl)phenyl)chloroborane (0.80 g, 1.7 mmol) is dissolved in 20 mL of toluene in a 110-mL glass jar. A Teflon-coated stir bar is added. In a 20-mL glass vial, Zn(C₆F₅)₂ (0.34 g, 0.85 mmol) is dissolved in 10 mL of toluene. The solution containing the zinc compound is added to the borane solution with stirring. A white solid precipitates upon completion of the addition. The reaction mixture is stirred at room temperature for 1 hour. An aliquot of the reaction mixture is removed, filtered, and analyzed by ¹⁹F NMR spectroscopy. The spectrum confirms that the reaction to form the desired product is present. The reaction mixture is filtered through a disposable PTFE frit to remove solids. The filtrate is then pumped down to dryness to yield a white solid. The solid is dissolved in the minimum amount of toluene required to get the material into solution and the solution is filtered again through a disposable PTFE frit. The toluene solution is placed in the glove box freezer (−40° C.) overnight, during which time fine, needle-like crystals precipitate. The crystals are collected by filtration, washed with cold pentane (−40° C.), and dried under vacuum for 1 hour. Total yield of bis(3,5-bis(trifluoromethyl)phenyl(2,3,4,5,6-pentafluorophenyl)borane: 0.74 g (72%).

In a second stage, in an N₂-purged glove box, 0.61 g (1.0 mmol) of bis(3,5-bis(trifluoromethyl)phenyl)(2,3,4,5,6-pentafluorophenyl)borane (prepared in stage 1) is weighed into a 110-mL glass jar and dissolved in 50 mL of THF. The THF is removed under vacuum with stirring to yield an oily white solid. The solid is triturated with 40 mL of pentane to yield a white solid. The white solid is characterized as the THF adduct of bis(3,5-bis(trifluoromethyl)phenyl)(2,3,4,5,6-pentafluorophenyl)borane. Yield: 0.51 g (75%).

Catalyst 2 is the THF adduct of bis(2,3,4,5,6-pentafluorophenyl)(3,5-bis(trifluoromethyl)phenyl)borane, which is prepared according to the following Schematic 8:

In particular, in a first stage, n-butyllithium (2.5 mL, 2.6 M in hexanes, 6.5 mmol) is added with stirring to a cold (between −101° C. and −99° C., CO₂(s), then N₂(l), methanol bath) solution of 1-bromo-2,3,4,5,6-pentafluorobenzene (1.68 g, 6.80 mmol) in diethyl ether (200 mL). The reaction mixture is stirred for 1 hour at −90° C.; a small amount of precipitate forms during this time. Then, (2,3,4,5,6-pentafluorophenyl)(3,5-bis(trifluoromethyl)phenyl)isopropoxyborane (3.00 g, 6.67 mmol) in ether (15 mL) is added slowly to the reaction mixture. The reaction mixture is stirred for 2 hours at −90° C., and then is allowed to warm to −78° C. and stirred for 2-3 more hours. The reaction mixture is allowed to warm to ambient temperature. The reaction mixture is filtered and the volatiles are removed under reduced pressure to give an oily precipitate containing a large amount of tiny crystals. The crystals are dissolved in THF (10 mL) and the volatiles are removed under reduced pressure to give a yellow oil. The oil is triturated with hexanes, but not all of the oil dissolves. The hexane solution is decanted off of the oil fraction. The volatiles are removed from the hexane solution and the oil fraction to give a white crystalline solid from the oil fraction (2.23 g) and a brownish solid from the hexane-soluble fraction (2.42 g). By multinuclear NMR spectroscopy, the white solid from the oil fraction is the desired product in pure form, lithium bis(tetrahydrofuranate) bis(2,3,4,5,6-pentafluorophenyl)-(3,5-bis(trifluoromethyl)phenyl)isopropoxyborate. By multinuclear NMR spectroscopy, the brownish solid is the desired product with some contaminants present. The brownish solid is washed twice with hexane to give a nearly white solid (2.35 g), which by NMR spectroscopy is characterized as the desired product, lithium bis(tetrahydrofuranate) bis(2,3,4,5,6-pentafluorophenyl)(3,5-bis(trifluoromethyl)phenyl)isopropoxyborate. Total yield: 4.58 g (91%).

In a second stage, to a solution of lithium bis(tetrahydrofuranate) bis(2,3,4,5,6-pentafluorophenyl)(3,5-bis(trifluoromethyl)phenyl)isopropoxyborate (4.40 g, 5.73 mmol) in diethyl ether (75 mL) is added hydrogen chloride solution in ether (4.0 mL, 2.0 M, 8.0 mmol) with gradual formation of precipitate observed. The reaction mixture is stirred for about 30 minutes, then the reaction mixture is stirred overnight under very slightly reduced pressure to remove volatiles to give a white solid. By ¹H NMR spectroscopy, it can be shown that isopropoxy groups are still present in the material isolated (starting material is still present). The white residue is dissolved in ether and additional hydrogen chloride solution (2.0 mL, 4.0 mmol) is added; only a trace of solid formation is observed. The reaction is stirred for 30 minutes and all volatiles are then removed under reduced pressure. By ¹H NMR spectroscopy, it can be shown that there is much less starting material contaminating the desired product. Next, the residue from the reaction mixture is dissolved in THF (10 mL) and the volatiles are again removed under reduced pressure. Toluene (50 mL) is added, the solution is filtered to remove LiCl, and the volatiles are removed overnight from the solution at a slow rate. By morning, the volatiles are not observed, leaving a white powder which by ¹H and ¹⁹F NMR spectroscopy is determined to be the desired product, the THF adduct of bis(2,3,4,5,6-pentafluorophenyl)(3,5-bis(trifluoromethyl)phenyl)borane. Yield of white powder: 3.09 g (86%).

Catalyst 3 is bis(3,5-bis(trifluoromethyl)phenyl)(3,4,5-trifluorophenyl)borane, which is prepared according to the following Schematic 9:

In a first stage, n-butyllithium (3.5 mL, 2.5 M in hexanes, 8.7 mmol) is added slowly dropwise with stirring to a cold (−75° C., CO₂(s) bath) solution of 1-bromo-3,5-bis(trifluoromethyl)benzene (2.77 g, 9.45 mmol) in diethyl ether (150 mL). The reaction mixture is stirred for 2 hours at −78° C. with formation of precipitate observed. A solution of (3,5-bis(trifluoromethyl)phenyl)(3,4,5-trifluorophenyl)isopropoxyborane (3.27 g, 7.89 mmol) in ether (15 mL) is added slowly. The reaction mixture is stirred for 1 hour, then the cold bath is removed from the now-clear solution to allow the mixture to warm to ambient temperature and stand overnight. Next, HCl solution (5.0 mL, 2 M in diethyl ether, 10 mmol) is added at ambient temperature and the reaction mixture is stirred overnight, filtered, and volatiles are removed under reduced pressure. The resultant solid is analyzed by ¹H NMR spectroscopy and can be found to still contain some isopropoxyborane starting material. The solid is dissolved in diethyl ether and additional HCl solution (2.0 mL, 4.0 mmol) is added. Next, the reaction mixture is filtered and the volatiles are removed under reduced pressure to give an oily solid. The residue is extracted with hot hexane, filtered, and the yellow solution is placed in the freezer (−35° C.) overnight and formation of solids is observed. The supernatant is drained off and the solid is dried under reduced pressure. Yield of beige solid (bis(3,5-bis(trifluoromethyl)phenyl)(3,4,5-trifluorophenyl)borane): 1.44 g (32%).

Catalyst 4 is the THF adduct of bis(3,5-bis(trifluoromethyl)phenyl)(2,6-difluorophenyl)borane, which is prepared according to Schematic 10.

In particular, in a first stage n-butyllithium (3.0 mL, 2.5 M in hexanes, 7.4 mmol) is added slowly dropwise to a cold (−78° C., CO₂(s) bath) solution of 1-bromo-2,6-difluorobenzene (1.46 g, 7.56 mmol) in diethyl ether (100 mL). The reaction mixture is stirred for 1 hour at −78° C. Then, bis(3,5-bis(trifluoromethyl)phenyl)isopropoxyborane (3.69 g, 7.44 mmol) in ether (10 mL) is added slowly. Precipitate forms while the reaction mixture is allowed to warm to ambient temperature. By the time the reaction mixture has reached room temperature, the precipitate is dissolved to give a clear solution that is stirred for several hours. The solution is filtered and the volatiles are removed under reduced pressure to give a crystalline-appearing solid. The solid is dissolved in a minimum of boiling ether and the solution is placed in the freezer. After cooling overnight, the supernatant is decanted from the crystals that have formed. The crystals are dried under reduced pressure. Yield of crystals of lithium bis(diethyletherate) bis(3,5-bis(trifluoromethyl)phenyl)(2,6-difluorophenyl)isopropoxyborate: 6.9 g (88%).

In a second stage, lithium bis(diethyletherate) bis(3,5-bis(trifluoromethyl)phenyl)(2,6-difluorophenyl)isopropoxyborate (5.85 g, 10.6 mmol) is dissolved in ether (150 mL). Then, chlorotrimethylsilane (3.0 mL, 24 mmol) is added at ambient temperature. Precipitate begins to form within 15 minutes. The reaction mixture is allowed to stir over the weekend. By Monday, the volatiles evaporate away (non-sealed container). The colorless solid is extracted with ether and filtered. The volatiles are removed under reduced pressure to give the diethyl ether adduct of bis(3,5-bis(trifluoromethyl)phenyl)(2,6-difluorophenyl)borane as a colorless solid, 4.9 grams (74%). NMR spectra shows clean product, but with only about 86% of the required ether for a monoetherate complex. The product is dissolved in ether to give a hazy solution. Then, THF (6 mL) is added and the solution becomes crystal clear. The volatiles are removed under reduced pressure to give a glassy solid. The solid is extracted with benzene, filtered, and the volatiles are removed under reduced pressure to give a white solid. The yield of the THF adduct of bis(3,5-bis(trifluoromethyl)phenyl)(2,6-difluorophenyl)borane is 4.6 g (94%).

Catalyst 5 is the THF adduct of bis(3,5-bis(trifluoromethyl)phenyl)(2-chloro-4,6-difluorophenyl)borane, which is prepared according to the following Schematic 11:

In particular, in a first stage, n-butyllithium (5.2 mL, 2.5 M in hexanes, 13 mmol) is added slowly dropwise to a cold (−78° C., CO₂(s) bath) solution of 1-bromo-2-chloro-4,6-difluorobenzene (3.03 g, 13.3 mmol) in diethyl ether (150 mL). The reaction mixture is stirred for 1 hour at −78° C. Then, bis(3,5-bis(trifluoromethyl)phenyl)isopropoxyborane (6.50 g, 13.1 mmol) in ether (15 mL) is added slowly. The reaction mixture is stirred for several hours, then is allowed to warm to ambient temperature while stirring overnight. The volatiles are removed under reduced pressure to give a solid. The solid is triturated with hexane and filtered. The solid is washed with hexane and dried under reduced pressure to give a yield of lithium(diethyletherate)_(1.5) bis(3,5-bis(trifluoromethyl)phenyl)(2-chloro-4,6-difluorophenyl)isopropoxyborate of 9.2 g (92%).

In a second stage, chlorotrimethylsilane (1.1 mL, 0.94 grams, 8.7 mmol) is added slowly dropwise to a solution of lithium(diethyletherate)_(1.5) bis(3,5-bis(trifluoromethyl)phenyl)(2-chloro-4,6-difluorophenyl)isopropoxyborate (prepared in stage 1, 4.73 g, 6.21 mmol) in diethyl ether (100 mL). Precipitate begins to form within an hour. The reaction mixture is allowed to stir overnight. The reaction mixture is filtered and the volatiles are removed under reduced pressure to give a pasty solid-containing residue, 4.0 g. The residue is extracted with benzene, the solution is filtered, and the volatiles are removed under reduced pressure to give a colorless solid, 3.60 g (99.1%). The solid is divided into two portions: about 1.5 g and 2.0 g. Then, THF (8 mL) is added to a solution of the 2.0 g portion in ether. The volatiles are removed under reduced pressure and the resulting solid is dissolved in ether (25 mL). The volatiles are again removed under reduced pressure to give the THF adduct of bis(3,5-bis(trifluoromethyl)phenyl)(2-chloro-4,6-difluorophenyl)borane as a crystalline solid (2.2 g, yield is quantitative).

Catalyst 6, is the THF adduct of bis(3,5-bis(trifluoromethyl)phenyl)(2,4,6-trifluorophenyl)borane, which is prepared according to the following Schematic 12:

In particular, in a first stage, in a N₂-purged glove box, 3.00 grams (14.2 mmol) of 1-bromo-2,4,6-trifluorobenzene is combined with 200 mL of diethyl ether in a 500-mL Schlenk flask. A Teflon-coated stir bar is added to the colorless solution and the flask is sealed with a rubber septum before being removed from the glove box. In a fume-hood, the flask is connected to a nitrogen line and placed in a dry ice/acetone bath (−78° C.) for 20 minutes to chill. A 2.5 M solution of n-butyllithium in hexane (5.8 mL, 14 mmol) is added via syringe to the cold solution. The reaction mixture is stirred at −78° C. for 1 hour. A solution of 7.05 g (14.2 mmol) of bis(3,5-bis(trifluoromethyl)phenyl)isopropoxyborane in 25 mL of diethyl ether is prepared in the glove box and drawn up into a syringe. The solution is injected slowly into the flask containing the cold aryllithium solution at −78° C. The reaction mixture is then allowed to slowly warm to room temperature while stirring overnight. The next morning, the solution is filtered from a small amount of precipitate that forms. The volatiles are removed under reduced pressure to give a pale yellow solid. The solid is extracted with hexane (2×100 mL), the resulting mixture is filtered, and the volatiles are removed under reduced pressure to give an off-white solid. The solid is triturated with hexane, the solids are filtered out, and the volatiles are removed under reduced pressure from the filtrate to give a white solid, lithium bis(diethyletherate) bis(3,5-bis(trifluoromethyl)phenyl)(2,4,6-trifluorophenyl)isopropoxyborate Yield: 10.6 g, (96%).

In a second stage, in a Na purged glove box, 8.00 g (10.2 mmol) of lithium bis(diethyletherate) bis(3,5-bis(trifluoromethyl)phenyl)(2,4,6-trifluorophenyl)isopropoxyborate from stage 1 is dissolved in 100 mL of diethyl ether to form a colorless solution. Chlorotrimethylsilane (3.2 mL, 2.7 g, 25 mmol) is added with stirring to the solution at room temperature. The mixture is allowed to stir overnight at room temperature with formation of copious precipitate. An aliquot of the reaction mixture is removed and analyzed by ¹⁹F NMR spectroscopy to confirm that the reaction has gone to completion. The reaction mixture is filtered through Celite to remove LiCl and the volatiles are removed under reduced pressure. The residue is extracted into benzene, the solution is filtered, and the volatiles are removed under reduced pressure to give a white powder. Multinuclear NMR spectroscopy confirms formation of bis(3,5-bis(trifluoromethyl)phenyl)(2,4,6-trifluorophenyl)borane in pure form. Yield: 4.99 g (86%).

In a third stage, in a N₂-purged glove box, 4.45 g (7.82 mmol) of bis(3,5-bis(trifluoromethyl)phenyl)(2,4,6-trifluorophenyl)borane from stage 2 is dissolved in ether (20 mL) and THF (2 mL) is added. The volatiles are removed under reduced pressure to give the product as a white solid. The white solid is characterized by multinuclear NMR spectroscopy as the mono-THF adduct of bis(3,5-bis(trifluoromethyl)phenyl)(2,4,6-trifluorophenyl)borane. Yield: 4.81 g (96%).

Catalyst 7 is the THF adduct of bis(3,5-bis(trifluoromethyl)phenyl)(2-fluoro-3-(trifluoromethyl)phenyl)borane, which is prepared according to the following Schematic 13:

In particular, in a first stage, n-butyllithium (5.0 mL, 2.5 M in hexanes, 13 mmol) is added slowly to a cold (−78° C., CO₂(s) bath) solution of 1-bromo-2-fluoro-3-(trifluoromethyl)benzene (3.11 g, 12.8 mmol) in diethyl ether (200 mL). The reaction mixture is stirred for 1 hour at −78° C. Then, bis(3,5-bis(trifluoromethyl)phenyl)isopropoxyborane (6.34 g, 12.8 mmol) in ether (15 mL) is added slowly. The reaction mixture is stirred for several hours at −78° C. The solution is allowed to warm to ambient temperature while stirring overnight to give a slightly cloudy yellow solution. The reaction mixture is filtered and the volatiles are removed to give a white solid. The solid is extracted with hexane, the solution is filtered, and the volatiles are removed slowly from the filtrate under reduced pressure to give large crystals. The supernatant is drained off, the crystals are washed with a small amount of hexane (5 mL), and the volatiles are removed under reduced pressure to give the product, lithium(diethyletherate) bis(3,5-bis(trifluoromethyl)phenyl)(2-fluoro-3-(trifluoromethyl)phenyl)isopropoxyborate, as large colorless crystals, with a yield of 8.67 g (92%).

In a second stage, to a solution of lithium(diethyletherate) bis(3,5-bis(trifluoromethyl)phenyl)(2-fluoro-3-(trifluoromethyl)phenyl)isopropoxyborate (from stage 1, 8.67 grams, 11.6 mmol) in ether (100 mL) is added chlorotrimethylsilane (2.0 mL, 1.7 g, 15.8 mmol) and the mixture is allowed to stir overnight. NMR analysis of an aliquot shows incomplete reaction; additional chlorotrimethylsilane (1.0 mL, 7.9 mmol) is added and the mixture is allowed to stir overnight. NMR analysis of an aliquot shows incomplete reaction; HCl solution (2.0 mL, 2 M in ether, 4.0 mmol) is added and the mixture is allowed to stir overnight. NMR analysis shows the reaction has gone to completion. The reaction mixture is filtered and the volatiles are removed under reduced pressure. The residue is extracted with benzene, the solution is filtered, and the volatiles are removed under reduced pressure to give a thick, yellow oil. The oil is extracted with hexane, the solution is filtered, and the volatiles are slowly removed under reduced pressure to give the free borane, bis(3,5-bis(trifluoromethyl)phenyl)(2-fluoro-3-(trifluoromethyl)phenyl)borane (6.0 g, 86%). The borane is dissolved in diethyl ether (10 mL), and tetrahydrofuran (10 mL) is added and the volatiles are removed to obtain the THF-adduct of bis(3,5-bis(trifluoromethyl)phenyl)(2-fluoro-3-(trifluoromethyl)phenyl)borane with a yield of 6.5 g (97%).

Catalyst 8 is the THF adduct of bis(3,5-bis(trifluoromethyl)phenyl)(2-fluoro-4-(trifluoromethyl)phenyl)borane, which is prepared according to the following Schematic 14:

In particular, in a first stage, n-butyllithium (5.0 mL, 2.54 M in hexanes, 12.7 mmol) is added quickly to a cold (−78° C., CO₂(s) bath) solution of 1-bromo-2-fluoro-4-(trifluoromethyl)benzene (3.08 g, 12.7 mmol) in diethyl ether (200 mL). The reaction mixture is stirred for 1 hour at −78° C. Bis(3,5-bis(trifluoromethyl)phenyl)isopropoxyborane (6.29 g, 12.7 mmol) in ether (15 mL) is added slowly to give a colorless solution. The reaction mixture is stirred for several hours, and then is allowed to warm to ambient temperature. By the time the temperature reaches about −50° C. the solution turns light yellow. The solution is stirred overnight to give a slightly cloudy yellow solution. The reaction mixture is filtered and the volatiles are removed to give a cloudy pale yellow oil. The oil is extracted with hexane, filtered, and the volatiles are removed to give a cloudy pale yellow oil. Yield of lithium bis(diethyletherate) bis(3,5-bis(trifluoromethyl)phenyl)(2-fluoro-4-(trifluoromethyl)phenyl)isopropoxyborate is 9.13 grams (88%). THF (10 mL) is added to dissolve the oil and to form the lithium bis(tetrahydrofuranate) borate salt. The volatiles are removed under reduced pressure overnight to yield lithium bis(tetrahydrofuranate) bis(3,5-bis(trifluoromethyl)phenyl)(2-fluoro-4-(trifluoromethyl)phenyl)isopropoxyborate (9.1 g, 88%).

In a second stage, to a solution of lithium bis(tetrahydrofuranate) bis(3,5-bis(trifluoromethyl)phenyl)(2-fluoro-4-(trifluoromethyl)phenyl)isopropoxyborate (9.1 g, 11 mmol) in ether (100 mL) is added chlorotrimethylsilane (2.0 mL, 1.7 grams, 15.8 mmol) and the mixture is allowed to stir overnight. The NMR analysis of an aliquot shows incomplete reaction; additional chlorotrimethylsilane (1.0 mL, 7.9 mmol) is added and the mixture is allowed to stir overnight. The NMR analysis of an aliquot shows incomplete reaction; HCl solution (2.0 mL, 2 M in ether, 4.0 mmol) is added and the mixture is allowed to stir overnight. Volatiles are removed from the reaction mixture and the resultant residue is extracted with benzene, the solution is filtered, and the volatiles are removed from the filtrate under reduced pressure to give a light yellow solid. The yellow solid is extracted with hexane, the solution is filtered, and the volatiles are slowly removed under reduced pressure to give large crystalline masses. The crystals are heated to 65° C. with hexane (20 mL). The mixture is allowed to cool. The yellow supernatant is discarded and the solids are dried under reduced pressure to yield bis(3,5-bis(trifluoromethyl)phenyl)(2-fluoro-4-(trifluoromethyl)phenyl)borane (6.22 g, 92%). The borane (6.22 g) is dissolved in diethyl ether (10 mL), tetrahydrofuran (10 mL) is added, and the volatiles are removed to obtain the THF-adduct of bis(3,5-bis(trifluoromethyl)phenyl)(2-fluoro-4-(trifluoromethyl)phenyl)borane as a light beige crystalline product. Yield: 6.76 g (96%).

Catalyst 9 is bis(3,5-bis(trifluoromethyl)phenyl)(2,3,4,5,6-pentachlorophenyl)borane, which is prepared according to the following Schematic 15:

In particular, in a first stage, n-butyllithium (5.0 mL, 2.5 M, 13 mmol) is added quickly dropwise to a cold (−78° C., CO₂(s) bath) solution of hexachlorobenzene (3.61 g, 12.7 mmol) in diethyl ether (150 mL). The reaction mixture is stirred for 30 minutes at −78° C. and then allowed to warm to −40° C. A bright yellow solution is obtained. The reaction mixture is cooled again to −78° C. and a solution of bis(3,5-bis(trifluoromethyl)phenyl)isopropoxyborane (6.29 g, 12.7 mmol) in diethyl ether (15 mL) is added slowly. The reaction mixture is stirred for 2-3 hours at −78° C., and then allowed to warm to ambient temperature and stir for another 2-3 hours. The reaction mixture is filtered through a disposable PTFE frit and volatiles are removed from the filtrate under reduced pressure. The resultant yellow residue is extracted with hot hexane and filtered to give a yellow solution. The yellow solution is allowed to cool to ambient temperature and a small amount of orange oil precipitates. The solution is decanted off the oil and placed in the freezer overnight (−33° C.) to yield more orange oil and pale yellow crystals. The supernatant solution is decanted from the oil and the crystals, and the oil/solid mixture is dried under reduced pressure. The crystals are physically separated from the dried oil and characterized as the desired product, lithium bis(diethyletherate) bis(3,5-bis(trifluoromethyl)phenyl)(2,3,4,5,6-pentachlorophenyl)isopropoxyborate. Yield: 2.34 g (21%).

In a second stage, a HCl solution (1.3 mL, 2.0 M in diethyl ether, 2.6 mmol) is added at ambient temperature to a solution of lithium bis(diethyletherate) bis(3,5-bis(trifluoromethyl)phenyl)(2,3,4,5,6-pentachlorophenyl)isopropoxyborate (1.3 g, 1.4 mmol) in diethyl ether (20 mL). A white precipitate forms immediately upon completion of the addition. The reaction mixture is stirred over the weekend at ambient temperature. The volatiles are removed from the reaction mixture under reduced pressure and the resultant pale yellow residue is washed with hexane (30 mL), and the mixture is filtered through a disposable PTFE frit. The residue remaining on the frit is extracted with ether, the solution is filtered, and the volatiles are removed from the filtrate to yield a very pale yellow solid. The solid is extracted with warm (45° C.) hexane (100 mL) and the mixture is filtered to give a yellow solution. The yellow solution is cooled overnight in the freezer (−33° C.) to yield small, colorless, block-shaped crystals. The supernatant solution is decanted from the crystals and the crystals are dried under reduced pressure to yield 0.79 g of bis(3,5-bis(trifluoromethyl)phenyl)(2,3,4,5,6-pentachlorophenyl)borane. The supernatant solution is concentrated and cooled overnight in the freezer to yield 0.082 grams of additional product. Total yield: 0.87 g (91%).

Catalyst 10 is the THF adduct of bis(3,5-bis(trifluoromethyl)phenyl)(2,5-bis(trifluoromethyl)phenyl)borane, which is prepared according to the following Schematic 16:

In particular, in a first stage, n-butyllithium (4.0 mL, 2.5 M in hexanes, 10 mmol) is added slowly to a cold (−78° C., CO₂(s) bath) solution of 1-bromo-2,5-bis(trifluoromethyl)benzene (3.00 g, 10.2 mmol) in diethyl ether (200 mL). The reaction mixture is stirred for 1 hour at −78° C. Bis(3,5-bis(trifluoromethyl)phenyl)isopropoxyborane (5.04 g, 10.2 mmol) in ether (18 mL) is added slowly to the reaction mixture and the solution is stirred for several hours at −78° C. The reaction mixture is allowed to warm to ambient temperature while stirring overnight to give a slightly yellow clear solution. The volatiles are removed from the reaction mixture to give a yellow oil. The oil is extracted with benzene. There is nothing insoluble. The volatiles are removed from the benzene solution to give the product, lithium(diethyletherate) bis(3,5-bis(trifluoromethyl)phenyl)(2,5-bis(trifluoromethyl)phenyl)isopropoxyborate, as a yellow oil. Yield: 7.88 g (98%).

In a second stage, lithium(diethyletherate) bis(3,5-bis(trifluoromethyl)phenyl)(2,5-bis(trifluoromethyl)phenyl)isopropoxyborate (7.88 g, 9.97 mmol) is dissolved in ether (150 mL). Chlorotrimethylsilane (2.6 mL, 20 mmol) is added. The reaction mixture is allowed to stir overnight to give a yellow solution with colorless precipitate. The volatiles are removed under reduced pressure. The residue is extracted with hexane (100 ml). The mixture is filtered and the volatiles are concentrated under reduced pressure. The solution is cooled in the freezer (−33° C.) overnight. The precipitate is filtered out and dried under reduced pressure to give the product, bis(3,5-bis(trifluoromethyl)phenyl)(2,5-bis(trifluoromethyl)phenyl)borane, as a white powder. Yield: 6.02 g (93%).

In a third stage, bis(3,5-bis(trifluoromethyl)phenyl)(2,5-bis(trifluoromethyl)phenyl)borane (4.83 g) is dissolved in ether (50 mL) and THF (6 mL) is added. The volatiles are removed slowly from the solution under reduced pressure to give the product, the THF adduct of bis(3,5-bis(trifluoromethyl)phenyl)(2,5-bis(trifluoromethyl)phenyl)borane, as a white solid: 5.0 g, 93%. Subjecting the THF complex to full vacuum easily removes the coordinated THF molecule.

Catalyst 11 is (3,5-bis(trifluoromethyl)phenyl)bis(2,5-bis(trifluoromethyl)phenyl)borane, which is prepared according to the following Schematic 17:

In particular, in a first stage, n-butyllithium (2.4 mL, 2.5 M in hexanes, 6.1 mmol) is added slowly to a cold (−78° C., CO₂(s) bath) solution of 1-bromo-2,5-bis(trifluoromethyl)benzene (1.80 g, 6.14 mmol) in diethyl ether (150 mL). The reaction mixture is stirred for 1 hour at −78° C. (2,5-Bis(trifluoromethyl)phenyl)(3,5-bis(trifluoromethyl)phenyl)isopropoxyborane (3.02 g, 6.09 mmol) in ether (18 mL) is added slowly. The reaction mixture is stirred for several hours at −78° C. The solution is allowed to warm to ambient temperature while stirring overnight to give a slightly yellow clear solution. The volatiles are removed from the reaction mixture to give a yellow oil. The oil is extracted with benzene. There is nothing insoluble to filter out. The volatiles are removed from the benzene solution to give the product, lithium(diethyletherate) bis(2,5-bis(trifluoromethyl)phenyl)(3,5-bis(trifluoromethyl)phenyl)isopropoxyborate, as a yellow oil. The yield is 4.21 g (87.6%).

In a second stage, chlorotrimethylsilane (1.1 mL, 10 mmol) is added to a solution of lithium(diethyletherate) bis(2,5-bis(trifluoromethyl)phenyl)(3,5-bis(trifluoromethyl)phenyl)isopropoxyborate (3.92 g, 4.95 mmol) in diethyl ether (150 mL) with stirring. Within 15 minutes precipitate is observed in solution. The reaction mixture is stirred overnight. The mixture is filtered and the volatiles are removed under reduced pressure to give a colorless solid, 3.26 g. The product is extracted with hexane, the solution isfiltered, and the volatiles are removed from the filtrate under reduced pressure to give the product, (3,5-bis(trifluoromethyl)phenyl)bis(2,5-bis(trifluoromethyl)phenyl)borane, as a pale solid. Yield: 3.11 g (97%).

Catalyst 12 is the THF adduct of bis(3,5-bis(trifluoromethyl)phenyl)(2,3,5,6-tetrafluoro-4-(trifluoromethyl)phenyl)borane, which is prepared according to the following Schematic 18:

In particular, in a first stage, n-butyllithium (3.0 mL, 2.5 M, 7.6 mmol) is added to a cold (between −101° C. and −99° C., CO₂(s), then N₂(l), methanol bath) solution of 1-bromo-2,3,5,6-tetrafluoro-4-(trifluoromethyl)benzene (2.26 g, 7.61 mmol) in diethyl ether (100 mL) with stirring. The reaction mixture is stirred for 2 hour at around −100° C. then is allowed to warm up to −78° C. Bis(3,5-bis(trifluoromethyl)phenyl)isopropoxyborane (3.78 g, 7.61 mmol) in ether (10 mL) is added slowly. The reaction mixture is allowed to warm to ambient temperature while stirring overnight. The pale yellow (nearly clear) solution is filtered and the volatiles are removed from the filtrate under reduced pressure to give a crystalline-appearing solid. The solid is washed with hexane, the mixture is filtered, and the solid is dried under reduced pressure. The yield of the colorless solid product, lithium(diethyletherate) bis(3,5-bis(trifluoromethyl)phenyl)(2,3,5,6-tetrafluoro-4-(trifluoromethyl)phenyl)isopropoxyborate, is 6.16 g (93%).

In a second stage, chlorotrimethylsilane (2.0 mL, 18 mmol) is added to lithium(diethyletherate) bis(3,5-bis(trifluoromethyl)phenyl)(2,3,5,6-tetrafluoro-4-(trifluoromethyl)phenyl)isopropoxyborate (6.16 g, 7.10 mmol) in diethyl ether (100 mL) with stirring. The reaction mixture is stirred overnight. NMR analysis shows that no reaction has occurred. Hydrogen chloride solution in ether (7.0 mL, 14 mmol) is added and the reaction mixture is stirred overnight. The mixture is filtered and the volatiles are removed from the filtrate under reduced pressure. The resultant residue is dissolved in toluene, the solution is filtered, and the volatiles are removed from the filtrate under reduced pressure to give 4.50 g of crude product. The colorless, pasty solid is suspended in hexane, the mixture is filtered, and the solid is dried under reduced pressure to give the product, the isopropanol adduct of bis(3,5-bis(trifluoromethyl)phenyl)(2,3,5,6-tetrafluoro-4-(trifluoromethyl)phenyl)borane, as a colorless powder. Yield: 2.45 g (53%).

In a third stage, the isopropanol adduct of bis(3,5-bis(trifluoromethyl)phenyl)(2,3,5,6-tetrafluoro-4-(trifluoromethyl)phenyl)borane (1.81 g, 2.54 mmol) is dissolved in ether (40 mL). THF (10 mL) is added to the solution. The solution is allowed to evaporate slowly to give large crystals. The supernatant is removed, the very pale yellow crystals are washed with hexane, and the crystals are dried under reduced pressure (1.08 g). The crystals are analyzed by x-ray crystallography to be the isopropanol adduct of bis(3,5-bis(trifluoromethyl)phenyl)(2,3,5,6-tetrafluoro-4-(trifluoromethyl)phenyl)borane. The supernatant and hexane washings are concentrated to give a second crop of crystals (0.42 g). The second crop of crystals is washed and dried in the same manner as the first crop. NMR analysis shows the presence of coordinated isopropanol and very little THF. THF is added to the second crop of crystals and the volatiles are removed under reduced pressure. NMR analysis shows the THF/isopropanol mole ratio to be 6.4:1. The solid is dissolved a second time in THF and the volatiles are removed under reduced pressure. NMR analysis shows the THF/isopropanol mole ratio to be 14:1. The solid is dissolved a third time in THF and the volatiles are removed under reduced pressure. NMR analysis shows the THF/isopropanol mole ratio to be 23:1. The solid is dissolved a fourth time in THF and the volatiles are removed under reduced pressure. The solid is dissolved a fifth time in THF and the volatiles are removed under reduced pressure to give the product, THF adduct of bis(3,5-bis(trifluoromethyl)phenyl)(2,3,5,6-tetrafluoro-4-(trifluoromethyl)phenyl)borane, as a colorless powder, 0.41 g (21% yield). NMR analysis shows the THF/isopropanol mole ratio to be 41:1, which is deemed sufficiently pure.

Catalyst 13 is the THF adduct of bis(3,5-bis(trifluoromethyl)phenyl)(2,4-difluoro-3-(trifluoromethyl)phenyl)borane, which is prepared according to the following Schematic 19:

In particular, in a first stage, n-butyllithium (4.5 mL, 2.5 M in hexanes, 11 mmol) is added slowly to a cold (−78° C., CO₂(s) bath) solution of 1-bromo-2,4-difluoro-3-(trifluoromethyl)benzene (2.98 g, 11.4 mmol) in diethyl ether (200 mL). The reaction mixture is stirred for 1.5 hours at −78° C. Bis(3,5-bis(trifluoromethyl)phenyl)isopropoxyborane (5.66 g, 11.4 mmol) in diethyl ether (15 mL) is added slowly. The reaction mixture is stirred for several hours at −78° C. The solution is allowed to warm to ambient temperature while stirring over the weekend to give a slightly cloudy yellow solution. The reaction mixture is filtered and the volatiles are removed to give a white solid. The solid is suspended in hexane, the mixture is filtered, and the solids on the frit are washed with hexane. The volatiles are removed under reduced pressure from the white solid collected on the frit (5.97 g) and from the washings. Large crystals form as the volatiles are removed from the washings. By NMR analysis the white solid collected on the frit is very pure desired product, lithium(diethyletherate) bis(3,5-bis(trifluoromethyl)phenyl)(2,4-difluoro-3-(trifluoromethyl)phenyl)isopropoxyborate, while the crystals obtained from the washings are nearly pure product. The crystals from the washings are heated with hexane to 60° C. (about half of the crystals dissolve) and placed in the freezer overnight. The supernatant is drained off and the solids are dried under reduced pressure to give a second crop: 1.66 g. Total yield of colorless product, lithium(diethyletherate) bis(3,5-bis(trifluoromethyl)phenyl)(2,4-difluoro-3-(trifluoromethyl)phenyl)isopropoxyborate, is 7.63 g (88%).

In a second stage, chlorotrimethylsilane (2.0 mL, 16 mmol) is added to a solution of lithium(diethyletherate) bis(3,5-bis(trifluoromethyl)phenyl)(2,4-difluoro-3-(trifluoromethyl)phenyl)isopropoxyborate (5.80 g, 7.65 mmol) in ether (150 mL). The reaction mixture is allowed to stir overnight. The volatiles are removed under reduced pressure. The residue is extracted with a mixture (1:1) of benzene/ether. The slurry is filtered and the volatiles are removed under reduced pressure to give the product, bis(3,5-bis(trifluoromethyl)phenyl)(2,4-difluoro-3-(trifluoromethyl)phenyl)borane, as a colorless powder. Yield: 4.67 g (99%).

In a third stage, bis(3,5-bis(trifluoromethyl)phenyl)(2,4-difluoro-3-(trifluoromethyl)phenyl)borane (3.84 g, 6.21 mmol) is dissolved in ether (50 mL) and THF (8 mL) is added. The volatiles are removed from the solution under reduced pressure. The residue is triturated with hexane, the mixture is filtered, and the volatiles are removed from the solid on the frit under reduced pressure to give the product as a white solid: 3.034 g. Additional product (0.65 g) is obtained from the hexane washings. Total: 3.68 g (86%).

Catalyst A is tris(pentafluorophenyl)borane, referred to as FAB, available from (available from Boulder Scientific).

Catalyst B is tris(bis(3,5-trifluoromethyl)phenyl)borane

Catalyst C is A zinc hexacyanocobaltate catalyst complex (available from Covestro under the name Arcol 3® Catalyst).

Preparation of Polyols

For preparing the polyols, the following materials are principally used:

P390 A starter compound that is a polyoxypropylene diol having a number average molecular weight of approximately 390 g/mol (available from The Dow Chemical Company as VORANOL ™ P 390). V2070 A polyoxypropylene triol having a number average molecular weight of approximately 700 g/mol, i.e., a low molecular weight PO triol (available from The Dow Chemical Company as VORANOL ™ 2070). V230-064 A polyoxypropylene triol having a number average molecular weight of approximately 2700 g/mol (available from The Dow Chemical Company as VORANOL ™ 230-064). Solvent A glycol diether that has no hydroxyl functionality (available from The Dow Chemical Company as PROGLYDE ™ DMM). Additive An acidifying agent that includes phosphoric acid.

In particular, the following reaction may be carried out in a continuous flow reactor using the Catalysts 1 to 13 as discussed above and in a manner shown below in exemplary Schematic 20, and in view of the conditions provided in Table 1:

The polyols of Working Examples 1 to 20 and Comparative Examples B and C may be prepared using P390 as the initiator, ethylene oxide (EO) as the monomer, and the Solvent according to the conditions outlined in Table 1, below. Referring to Table 1, the EO binding enthalpy, and activation barrier to aldehyde are determined according to the computational methods discussed below.

TABLE 1 EO Activation Catalyst binding barrier to Con. Time Temp enthalpy aldehyde Catalyst (ppm) (Min) (° C.) (kcal/mol) (kcal/mol) Ex. A — — 10 90 n/a n/a Ex. B A 1000 10 90 −12.2 3.2 Ex. C 20 Ex. 1  1 1000 10 90 −12.6 5.0 Ex. 2 20 Ex. 3  2 1000 10 90 −12.9 3.8 Ex. 4 20 Ex. 5  3 1000 10 90 −11.3 7.3 Ex. 6 20 Ex. 7  4 1000 10 90 −11.4 6.7 Ex. 8 20 Ex. 9  5 1000 10 90 −10.1 6.1 Ex. 10 20 Ex. 11  6 1000 10 90 −10.9 6.0 Ex. 12 20 Ex. 13  7 1000 10 90 −12.7 6.3 Ex. 14 20 Ex. 15  8 1000 10 90 −14.6 6.4 Ex. 16 20 Ex. 17 10 1000 10 90  −9.5 9.0 Ex. 18 20 Ex. 19 13 1000 10 90 −12.5 5.7 Ex. 20 20

Comparative example A is a negative control that may be run without catalyst. This example may be carried out by mixing the initiator and ethylene oxide in the tubular reactor at 90° C. for 10 min.

The polyol samples for Working Examples 1 to 20 and Comparative Examples B and C, may be prepared in a continuous flow reactor that is a microreactor available from Vapourtec Inc. can be used. For the examples, neat EO monomer may be fed to a pump via a pressure cylinder at 50 psig. A solvent reservoir containing the Solvent may be connected to another pump. A 2 mL injection loop may be utilized to introduce a solution of the specified catalyst and initiator (as 60 wt % of P390 in dipropylene glycol dimethyl ether) into the system. By controlling the flow rate, the catalyst and starter are introduced into the flow system at a defined rate. The EO monomer and initiator-catalyst-Solvent solution are combined at a mixing unit and fed into a 2 mL stainless steel coiled reactor. A back pressure regulator set at 250 psig may be used to control the system pressure and assist the EO to remain in a liquid phase. The continuous pressure reactor may be charged with 0.1 mL/min of the initiator-catalyst-Solvent mixture. The ethylene oxide may be fed to the reactor at a constant feed rate of 0.1 mL/min. Once the initiator-catalyst-Solvent mixture is introduced into the sample loop, the first 5.13 mL of the product mixture may be diverted to a scrubber consisting of 3 wt % aqueous potassium hydroxide. The next 3.04 mL of product mixture may be collected and analyzed by MALDI spectrometry.

The Temperature in Table 1 is the temperature in the reactor. The Time is residence time, which is defined as follows:

${{residence}\mspace{14mu} {time}} = \frac{{reactor}\mspace{14mu} {volume}}{\left( {{{flow}\mspace{14mu} {rate}\mspace{14mu} {of}\mspace{14mu} {pump}\mspace{14mu} A} + {{flow}\mspace{14mu} {rate}\mspace{14mu} {of}\mspace{14mu} {pump}\mspace{14mu} B}} \right)}$

When the flow rates of pumps A and B are 0.1 mL/min,

${{residence}\mspace{14mu} {time}} = {\frac{2\mspace{14mu} {mL}}{\left( {{0.1} + 0.1} \right){{mL}/\min}} = {10\mspace{14mu} \min}}$

When the flow rates of pumps A and B are 0.05 mL/min,

${{residence}\mspace{14mu} {time}} = {\frac{2\mspace{14mu} {mL}}{\left( {0.05 + 0.05} \right){{mL}/\min}} = {20\mspace{14mu} \min}}$

The number-average molecular weight (Mn) achieved in the polymerization reaction may depend on the amount of volatile side-products (e.g. acetaldehyde) formed. For example, higher levels of volatile side-products may result in a Mn that is significantly lower than the theoretical Mn. Conversely, low levels of volatile side-products may help achieve a Mn that is close to the theoretical Mn. It may be desirable to achieve a Mn that is close to the theoretical Mn.

The PDI is defined as the ratio of the weight-average molecular weight (Mw) to the number-average molecular weight (Mn). The PDI may represent a measure of the extent of acetal coupling, as this reaction may effectively double the molecular weight. Accordingly, a comparison of the PDI at similar Mn values may provide a measure of the selectivity of a catalyst for alkoxylation (intended reaction) versus isomerization and acetalization. Lower PDI may be preferable for higher chemoselectivity.

The EO binding enthalpy is calculated relative to a resting state consisting of the free catalyst (where R⁴ is not present) and EO. Favorable binding (higher negative values, for example greater than −9.0 kcal/mol, greater than −10.0 kcal/mol, etc) is preferable for higher activity. Referring to Table 1, it is seen that calculations on Catalysts 1 and 2 provide a favorable EO binding enthalpy such that favorable activity is realized. Another measure of activity is the ring opening barrier shown below. Lower ring opening barriers are preferable for higher activity.

The activation barrier to aldehydes determines the amount of aldehyde and acetal formed, as shown below. Higher activation barriers are preferable for lower levels of aldehyde and subsequent acetal formation.

Referring to Working Examples 1 to 20 and Comparative Examples B and C, it is found that the activation barrier to undesired products (in comparison to the activation barrier for the desired EO content polyether polyol) may be significantly higher for Catalysts 1 to 8, 10 and 13 compared to Catalyst A. As such, it is unexpectedly found that the structures of Catalysts 1 to 8, 10 and 13 allow for increased yield of the desired product, as compared to Catalyst A.

Additional, Working Examples 21 to 29 and Comparative Examples C, D and E are carried out in a semi-batch process using varying initiators and monomers, using the Catalysts specified below, and in view of conditions provided in Tables 2 to 8 and according to Schematic 21:

Referring to Tables 2 to 8, Init refers to the initiator used, Mon refers to the monomer used, and M/I refers to the ratio of the monomer to initiator used. The monomers used are ethylene oxide (EO), or propylene oxide (PO)-ethylene oxide (EO) co-feed, or propylene oxide (PO) followed by ethylene oxide (EO) cap, or butylene oxide (BO) followed by ethylene oxide (EO) cap.

TABLE 2 (EO feed) Catalyst M/I Cata- Con. Temp Yield Init Mon ratio lyst (ppm) (° C.) Mn PDI (%) Ex. C P390 EO 10 A 250 55 790 1.36 60 Ex. 21 P390 EO 10 10 250 55 929 1.28 81

TABLE 3 (EO feed) Catalyst M/I Cata- Con. Temp Yield Init Mon ratio lyst (ppm) (° C.) Mn PDI (%) Ex. D P390 EO 10 A 500 55  888 1.49 79 Ex. 22 P390 EO 10  6 500 55  992 1.10 92 Ex. 23 P390 EO 10  8 500 55  948 1.27 87 Ex. 24 P390 EO 10 13 500 55 1054 1.18 87

TABLE 4 (PO, EO co-feed) Catalyst Mon Mon Cata- Con. Temp Yield Init 1 2 lyst (ppm) (° C.) Mn PDI (%) Ex. 25 P390 PO EO 10 250 90 924 1.08 91

TABLE 5 (PO, EO co-feed) Cata- lyst Mon Mon Cata- Con. Temp Yield Init 1 2 lyst (ppm) (° C.) Mn PDI (%) Ex. E P390 PO EO A 250 55 2112 1.23 90 Ex. 26 P390 PO EO 10 250 55 2190 1.08 94

TABLE 6 (PO, EO co-feed) Catalyst Mon Mon Cata- Con. Temp Yield Init 1 2 lyst (ppm) (° C.) Mn PDI (%) Ex. V230- PO EO 10 250 55 4956 1.15 89 27 064

TABLE 7 (PO then EO cap) Cata- lyst Mon Mon Cata- Con. Temp Yield Init 1 2 lyst (ppm) (° C.) Mn PDI (%) Ex. 28 V2070 PO EO 6 500 55 3864 1.14 94

TABLE 8 (BO then EO cap) Cata- lyst Mon Mon Cata- Con. Temp Yield Init 1 2 lyst (ppm) (° C.) Mn PDI (%) Ex. 29 P390 BO EO 6 500 55 1931 1.07 ~100

For Working Examples 21 to 29 and Comparative Example C, D and E the percent yield of the desired product in the resultant polyol samples is measured (based on a total weight of the resultant polyol samples). Referring to Tables 2 to 8, it is seen that the yield of the desired product is significantly higher when using catalysts according to exemplary embodiments, as compared to Catalyst A.

With respect to Table 9, it may be desirable to have a higher primary hydroxyl content. Additional working Examples 30 and 31 and Comparative Example F are carried out in a semi-batch process using the Catalysts specified below, in view of conditions provided in Table 9. Referring to Table 9, Init refers to the initiator used, Mon refers to the monomer used, and M/I refers to the ratio of the monomer to initiator used.

TABLE 9 Catalyst M/I Con. Temp 1° OH Init Mon ratio Catalyst (ppm) (° C.) (%) Ex. F P390 PO 27.5 B 250 55 45 Ex. 30 P390 PO 27.5 10 250 55 50 Ex. 31 P390 PO 27.5 11 250 55 65

Referring to Table 9, it is seen that the primary hydroxyl content at the end of the PO polymerization step is significantly higher for Catalysts 10 and 11 compared to Catalyst B. As compared to Catalyst B, it is believed that the addition of a different fluoroalkyl-substituted phenyl group and/or a different fluoro/chloro-substituted phenyl group serves to improve the primary hydroxyl content in the final polyol.

For the semi-batch alkoxylation reactions, the initiator was dried and charged into the pressure reactor using one of three procedures.

Procedure A: A stainless steel cylinder was dried in the oven at 125° C. for 6 h. The cylinder was cooled under a stream of nitrogen. The empty Parr reactor was dried at 140° C. jacket temperature under a nitrogen purge for 1 h. The initiator was dried in glassware at 110° C. for 2 h under a vacuum of 65 mbar and then transferred to the stainless steel cylinder under vacuum. The cylinder was weighed and its contents were transferred to the Parr reactor using nitrogen pressure. The cylinder was weighed after transfer to determine the amount charged to the Parr reactor.

Procedure B: The initiator was charged directly to the Parr reactor via a funnel. Drying was performed in the reactor for 120 min at 120° C. under a nitrogen purge.

Procedure C: The initiator was charged directly to the Parr reactor via a funnel. Drying was performed in the reactor for 180 min at 140° C. under a nitrogen purge.

Comparative Example C (Table 2): A 600 mL pressure reactor is charged with 66.8 grams of VORANOL™ P390, a poly(propylene oxide) triol of number-average molecular weight 400, using Procedure A. A solution of catalyst A (42 mg) in anhydrous tetrahydrofuran (2 mL) is added in one portion through a sample addition port under a nitrogen purge. After purging for 5 min, the nitrogen purge is stopped and the reactor vent is closed. Nitrogen is added through the reactor inlet to inert the headspace. Ethylene oxide (100.1 g) is added to the reactor at a reaction temperature of 55° C. and a constant feed rate of 0.75 g/min. Upon completion of ethylene oxide feed, the reaction mixture is allowed to digest for 35 min at 55° C. The reactor is vented and the reaction mixture is heated to 90° C. and purged for 30 minutes. The reaction mixture is cooled to 60° C. and the product is collected (100.2 g, 60%). Number-average molecular weight=790 (by gel permeation chromatography); Polydispersity index (PDI)=1.36 (by gel permeation chromatography).

Working Example 21 (Table 2): A 600 mL pressure reactor is charged with 63.1 grams of VORANOL™ P390, a poly(propylene oxide) triol of number-average molecular weight 400, using Procedure A. A solution of catalyst 10 (38 mg) in anhydrous tetrahydrofuran (2 mL) is added in one portion through a sample addition port under a nitrogen purge. After purging for 5 min, the nitrogen purge is stopped and the reactor vent is closed. Nitrogen is added through the reactor inlet to inert the headspace. Ethylene oxide (90.3 g) is added to the reactor at a reaction temperature of 55° C. and a constant feed rate of 0.75 g/min. Upon completion of ethylene oxide feed, the reaction mixture is allowed to digest for 35 min at 55° C. The reactor is vented and the reaction mixture is heated to 90° C. and purged for 35 minutes. The reaction mixture is cooled to 60° C. and the product is collected (124 g, 81%). Number-average molecular weight=929 (by gel permeation chromatography); Polydispersity index (PDI)=1.28 (by gel permeation chromatography).

Comparative Example D (Table 3): A 600 mL pressure reactor is charged with 55.2 grams of VORANOL™ P390, a poly(propylene oxide) triol of number-average molecular weight 400, using Procedure A. A solution of catalyst A (70 mg) in anhydrous tetrahydrofuran (2 mL) is added in one portion through a sample addition port under a nitrogen purge. After purging for 5 min, the nitrogen purge is stopped and the reactor vent is closed. Nitrogen is added through the reactor inlet to inert the headspace. Ethylene oxide (84.3 g) is added to the reactor at a reaction temperature of 55° C. and a constant feed rate of 0.75 g/min. Upon completion of ethylene oxide feed, the reaction mixture is allowed to digest for 50 min at 55° C. The reactor is vented and the reaction mixture is heated to 90° C. and purged for 30 minutes. The reaction mixture is cooled to 60° C. and the product is collected (111.1 g, 79%). Number-average molecular weight=888 (by gel permeation chromatography); Polydispersity index (PDI)=1.49 (by gel permeation chromatography).

Working Example 22 (Table 3): A 600 mL pressure reactor is charged with 59.7 grams of VORANOL™ P390, a poly(propylene oxide) triol of number-average molecular weight 400, using Procedure A. A solution of catalyst 6 (75 mg) in anhydrous tetrahydrofuran (2 mL) is added in one portion through a sample addition port under a nitrogen purge. After purging for 5 min, the nitrogen purge is stopped and the reactor vent is closed. Nitrogen is added through the reactor inlet to inert the headspace. Ethylene oxide (89.3 g) is added to the reactor at a reaction temperature of 55° C. and a constant feed rate of 0.75 g/min. Upon completion of ethylene oxide feed, the reaction mixture is allowed to digest for 65 min at 55° C. The reactor is vented and the reaction mixture is heated to 90° C. and purged for 30 minutes. The reaction mixture is cooled to 60° C. and the product is collected (136.6 g, 92%). Number-average molecular weight=992 (by gel permeation chromatography); Polydispersity index (PDI)=1.10 (by gel permeation chromatography).

Working Example 23 (Table 3): A 600 mL pressure reactor is charged with 63.5 grams of VORANOL™ P390, a poly(propylene oxide) triol of number-average molecular weight 400, using Procedure A. A solution of catalyst 8 (79 mg) in anhydrous tetrahydrofuran (2 mL) is added in one portion through a sample addition port under a nitrogen purge. After purging for 5 min, the nitrogen purge is stopped and the reactor vent is closed. Nitrogen is added through the reactor inlet to inert the headspace. Ethylene oxide (95.7 g) is added to the reactor at a reaction temperature of 55° C. and a constant feed rate of 0.75 g/min. Upon completion of ethylene oxide feed, the reaction mixture is allowed to digest for 20 min at 55° C. The reactor is vented and the reaction mixture is heated to 90° C. and purged for 30 minutes. The reaction mixture is cooled to 60° C. and the product is collected (138.4 g, 87%). Number-average molecular weight=948 (by gel permeation chromatography); Polydispersity index (PDI)=1.27 (by gel permeation chromatography).

Working Example 24 (Table 3): A 600 mL pressure reactor is charged with 59.7 grams of VORANOL™ P390, a poly(propylene oxide) triol of number-average molecular weight 400, using Procedure A. A solution of catalyst 13 (75 mg) in anhydrous tetrahydrofuran (2 mL) is added in one portion through a sample addition port under a nitrogen purge. After purging for 5 min, the nitrogen purge is stopped and the reactor vent is closed. Nitrogen is added through the reactor inlet to inert the headspace. Ethylene oxide (95.0 g) is added to the reactor at a reaction temperature of 55° C. and a constant feed rate of 0.75 g/min. Upon completion of ethylene oxide feed, the reaction mixture is allowed to digest for 50 min at 55° C. The reactor is vented and the reaction mixture is heated to 90° C. and purged for 30 minutes. The reaction mixture is cooled to 60° C. and the product is collected (137.1 g, 87%). Number-average molecular weight=1054 (by gel permeation chromatography); Polydispersity index (PDI)=1.18 (by gel permeation chromatography).

Working Example 25 (Table 4): A 600 mL pressure reactor is charged with 59.8 grams of VORANOL™ P390, a poly(propylene oxide) triol of number-average molecular weight 400, using Procedure B. A solution of catalyst 10 (37 mg) in anhydrous tetrahydrofuran (2 mL) is added in one portion through a sample addition port under a nitrogen purge. After purging for 5 min, the nitrogen purge is stopped and the reactor vent is closed. Propylene oxide (44.9 g) is added to the reactor at a reaction temperature of 90° C. and a constant feed rate of 0.75 g/min. Upon completion of propylene oxide feed, the reaction is allowed to digest for 20 min at 90° C. The reactor is vented and closed. Propylene oxide and ethylene oxide were co-fed at feed rates of 0.75 and 0.2 g/min, respectively. After addition of propylene oxide (36.0 g) and ethylene oxide (9.5 g), the reaction mixture is allowed to digest for 35 min at 90° C. The reactor is vented and purged with nitrogen for 30 min. The reaction mixture is cooled to 60° C. and the product is collected (135.9 g, 91%). Number-average molecular weight=924 (by gel permeation chromatography); Polydispersity index (PDI)=1.08 (by gel permeation chromatography).

Comparative Example E (Table 5): A 600 mL pressure reactor is charged with 65.9 grams of VORANOL™ P390, a poly(propylene oxide) triol of number-average molecular weight 400, using Procedure A. A solution of catalyst A (82 mg) in anhydrous tetrahydrofuran (2 mL) is added in one portion through a sample addition port under a nitrogen purge. After purging for 5 min, the nitrogen purge is stopped and the reactor vent is closed. Propylene oxide (165 g) is added to the reactor at a reaction temperature of 55° C. and a constant feed rate of 1.25 g/min. Upon completion of propylene oxide feed, the reaction is allowed to digest for 30 min at 55° C. The reactor is vented and closed. Propylene oxide and ethylene oxide were co-fed at feed rates of 1.0 and 0.25 g/min, respectively. After addition of propylene oxide (79.4 g) and ethylene oxide (19.9 g), the reaction mixture is allowed to digest for 20 min at 90° C. The reactor is vented and the reaction mixture is heated to 90° C. and purged for 30 minutes. The reaction mixture is cooled to 60° C. and the product is collected (296.4 g, 90%). Number-average molecular weight=2112 (by gel permeation chromatography); Polydispersity index (PDI)=1.23 (by gel permeation chromatography).

Working Example 26 (Table 5): A 600 mL pressure reactor is charged with 60.5 grams of VORANOL™ P390, a poly(propylene oxide) triol of number-average molecular weight 400, using Procedure A. A solution of catalyst 10 (76 mg) in anhydrous tetrahydrofuran (2 mL) is added in one portion through a sample addition port under a nitrogen purge. After purging for 5 min, the nitrogen purge is stopped and the reactor vent is closed. Propylene oxide (151.5 g) is added to the reactor at a reaction temperature of 55° C. and a constant feed rate of 1.25 g/min. Upon completion of propylene oxide feed, the reaction is allowed to digest for 20 min at 55° C. The reactor is vented and closed. Propylene oxide and ethylene oxide were co-fed at feed rates of 1.0 and 0.25 g/min, respectively. After addition of propylene oxide (73.3 g) and ethylene oxide (18.1 g), the reaction mixture is allowed to digest for 20 min at 90° C. The reactor is vented and the reaction mixture is heated to 90° C. and purged for 30 minutes. The reaction mixture is cooled to 60° C. and the product is collected (285 g, 94%). Number-average molecular weight=2190 (by gel permeation chromatography); Polydispersity index (PDI)=1.08 (by gel permeation chromatography).

Working Example 27 (Table 6): A 600 mL pressure reactor is charged with 240 grams of VORANOL™ 230-064, a poly(propylene oxide) triol of number-average molecular weight 2700, using Procedure A. A solution of catalyst 10 (111 mg) in anhydrous tetrahydrofuran (2 mL) is added in one portion through a sample addition port under a nitrogen purge. After purging for 5 min, the nitrogen purge is stopped and the reactor vent is closed. Propylene oxide (103.1 g) is added to the reactor at a reaction temperature of 55° C. and a constant feed rate of 1.25 g/min. Upon completion of propylene oxide feed, the reaction is allowed to digest for 15 min at 55° C. The reactor is vented and closed. Propylene oxide and ethylene oxide were co-fed at feed rates of 0.85 and 0.4 g/min, respectively. After addition of propylene oxide (65.1 g) and ethylene oxide (30.1 g), the reaction mixture is allowed to digest for 30 min at 55° C. The reactor is vented and the reaction mixture is heated to 90° C. and purged for 30 min. The reaction mixture is cooled to 60° C. and the product is collected (396.7 g, 89%). Number-average molecular weight=4956 (by gel permeation chromatography); Polydispersity index (PDI)=1.15 (by gel permeation chromatography).

Working Example 28 (Table 7): A 600 mL pressure reactor is charged with 56.6 grams of VORANOL™ 2070, a poly(propylene oxide) triol of number-average molecular weight 700, using Procedure C. A solution of catalyst 6 (200 mg) in anhydrous tetrahydrofuran (2 mL) is added in one portion through a sample addition port under a nitrogen purge. After purging for 5 min, the nitrogen purge is stopped and the reactor vent is closed. Propylene oxide (376 mL) is added to the reactor at a reaction temperature of 55° C. and a constant feed rate of 2.0 mL/min. Upon completion of propylene oxide feed, the reaction mixture is allowed to digest for 20 min at 55° C. The reaction mixture is vented and nitrogen is added to inert the headspace. Ethylene oxide (32 g) is added to the reactor at a reaction temperature of 55° C. and a constant feed rate of 0.75 g/min. Upon completion of ethylene oxide feed, the reaction is allowed to digest for 27 min at 55° C. The reactor is vented and the reaction mixture is heated to 90° C. and purged for 30 minutes. The reaction mixture is cooled to 60° C. and the product is collected (377.7 g, 94%). Number-average molecular weight=3864 (by gel permeation chromatography); Polydispersity index (PDI)=1.14 (by gel permeation chromatography).

Working Example 29 (Table 8): A 500 mL pressure reactor is charged with 65.0 grams of VORANOL™ P390, a poly(propylene oxide) diol of number-average molecular weight 400, using Procedure C. A solution of catalyst 6 (163 mg) in anhydrous tetrahydrofuran (2 mL) is added in one portion through a sample addition port under a nitrogen purge. After purging for 5 min, the nitrogen purge is stopped and the reactor vent is closed. Butylene oxide (231.1 g) is added to the reactor at a reaction temperature of 55° C. and a constant feed rate of 1.25 g/min. Upon completion of butylene oxide feed, the reaction is allowed to digest for 20 min at 55° C. Ethylene oxide (28.6 g) is added to the reactor at a reaction temperature of 55° C. and a constant feed rate of 0.75 g/min. Upon completion of ethylene oxide feed, the reaction is allowed to digest for 45 min at 55° C. The reaction mixture is vented and nitrogen is added to inert the headspace. The reaction mixture is purged at 90° C. for 30 minutes, cooled to 60° C. and the product is collected (325 g, 100%). Number-average molecular weight=1931 (by gel permeation chromatography); Polydispersity index (PDI)=1.07 (by gel permeation chromatography)

Comparative Example F (Table 9): A 600 mL pressure reactor is charged with 60.7 grams of VORANOL™ P390, a poly(propylene oxide) diol of number-average molecular weight 400, using Procedure C. A solution of Catalyst B (76 mg) in anhydrous tetrahydrofuran (2 mL) is added in one portion through a sample addition port under a nitrogen purge. After purging for 5 min, the nitrogen purge is stopped and the reactor vent is closed. Propylene oxide (294.9 mL) is added to the reactor at a reaction temperature of 55° C. and a constant feed rate of 1.5 mL/min. Upon completion of propylene oxide feed, the reaction is allowed to digest for 25 min at 55° C. The reaction mixture is vented and heated to 90° C. under a nitrogen purge. The reaction mixture is purged at 90° C. for 30 minutes, cooled to 60° C., and the product is collected (292.4 g, 98%). Number-average molecular weight=2060 (by gel permeation chromatography); Polydispersity index (PDI)=1.08 (by gel permeation chromatography); primary hydroxyl content=45% (by derivatization with trifluoroacetic anhydride followed by ¹⁹F NMR spectroscopy).

Working Example 30 (Table 9): A 600 mL pressure reactor is charged with 67.3 grams of VORANOL™ P390, a poly(propylene oxide) diol of number-average molecular weight 400, using Procedure A. A solution of Catalyst 10 (84 mg) in anhydrous tetrahydrofuran (2 mL) is added in one portion through a sample addition port under a nitrogen purge. After purging for 5 min, the nitrogen purge is stopped and the reactor vent is closed. Propylene oxide (269.5 g) is added to the reactor at a reaction temperature of 55° C. and a constant feed rate of 1.25 g/min. Upon completion of propylene oxide feed, the reaction is allowed to digest for 20 min at 55° C. The reaction mixture is vented and heated to 90° C. under a nitrogen purge. The reaction mixture is purged at 90° C. for 30 minutes, cooled to 60° C., and the product is collected (315 g, 94%). Number-average molecular weight=2157 (by gel permeation chromatography); Polydispersity index (PDI)=1.05 (by gel permeation chromatography); primary hydroxyl content=50% (by derivatization with trifluoroacetic anhydride followed by ¹⁹F NMR spectroscopy).

Working Example 31 (Table 9): A 600 mL pressure reactor is charged with 67.5 grams of VORANOL™ P390, a poly(propylene oxide) diol of number-average molecular weight 400, using Procedure A. A solution of Catalyst 11 (84 mg) in anhydrous tetrahydrofuran (2 mL) is added in one portion through a sample addition port under a nitrogen purge. After purging for 5 min, the nitrogen purge is stopped and the reactor vent is closed. Propylene oxide (269.9 g) is added to the reactor at a reaction temperature of 55° C. and a constant feed rate of 1.25 g/min. Upon completion of propylene oxide feed, the reaction is allowed to digest for 20 min at 55° C. The reaction mixture is vented and heated to 90° C. under a nitrogen purge. The reaction mixture is purged at 90° C. for 30 minutes, cooled to 60° C., and the product is collected (313.4 g, 93%). Number-average molecular weight=2102 (by gel permeation chromatography); Polydispersity index (PDI)=1.06 (by gel permeation chromatography); primary hydroxyl content=65% (by derivatization with trifluoroacetic anhydride followed by ¹⁹F NMR spectroscopy).

A process for the preparation of a polyether polyol may be carried out in a continuous or semi-batch process using a sequential dual catalyst process, similar to International Publication No. WO 2016/064698, which is incorporated by reference.

The analytical methods used with respect to the examples are described below:

Determination of M_(n) for semibatch products: Gel Permeation Chromatography (GPC) analysis is used for determination of number average molecular weight (Mn), which is carried out at a flow rate of 1.0 mL/min using four PLgel organic GPC columns connected in series (3 μm, Agilent Inc.) and tetrahydrofuran as eluent. The column temperature is 40° C. VORANOL™ CP 6001, VORANOL™ 210, 230-660, and 230-056N are used as standards.

Percent yield determination of semibatch reaction:

${{yield}\mspace{14mu} (\%)} = {\frac{\begin{matrix} {{weight}\mspace{14mu} {of}\mspace{14mu} {product}\mspace{14mu} {after}\mspace{14mu} {purging}\mspace{14mu} {with}\mspace{14mu} {nitrogen}} \\ {{at}\mspace{14mu} 90^{{^\circ}}\mspace{11mu} {C.\mspace{11mu} {for}}\mspace{14mu} 30\mspace{14mu} \min} \end{matrix}}{{theoretical}\mspace{14mu} {weight}\mspace{14mu} {of}\mspace{11mu} {product}\mspace{14mu} {based}\mspace{14mu} {on}\mspace{14mu} \frac{M}{I}{ratio}} \times 100}$

Computational Methodology for determination of binding enthalpy and activation barrier to aldehyde: The structures of all the species in ground and transition states are optimized using Density Functional Theory (DFT) at B3LYP/6-31+g** level (e.g., see Becke, A. D., J. Chem. Phys. 1993, 98, 5648; Lee, C. et al., Phys. Rev B 1988, 37, 785; and Miehlich, B. et al. Chem. Phys. Lett. 1989, 157, 200; Ditchfield, R. et al., J. Chem. Phys. 1971, 54, 724; Hehre, W. J. et al., J. Chem. Phys. 1972, 56, 2257; and Gordon, M. S. Chem. Phys. Lett. 1980, 76, 163). The effect of dielectric medium was included by using conductor like polarizable continuum model (CPCM), where diethylether (ε=4.2) was used as the medium of choice. The dispersion interactions are included by using D3 version of Grimmae along with Becke-Johnson damping. The vibrational analysis on the ground state geometries was performed and the lack of imaginary frequencies was used to ascertain the minima in the potential energy surface (PES). The same analysis on the transition state geometries indicated one imaginary frequency. In the latter case, the GaussView program was used to visualize the vibrational mode with imaginary frequency in order to ensure that the atoms moved along the desired reaction coordinate. For both ground state and transition state geometries, the vibrational analysis was used to compute the enthalpy (H₂₉₈) at 298 K by augmenting zero point energy to the electronic energy. All calculations were performed using G09 suit of programs. Computed enthalpies of binding (BH) with ethylene oxide (EO) and hydride shift to form aldehyde (ΔH₃ ^(‡)) in the ring opened conformation are listed in Table 1. It is hypothesized that strong binding enthalpy (large −ve number) is required for high activity of the borane catalyst. In addition, high ΔH₃ ^(‡) is desirable to avoid acetal formation, leading to high chemoselectivity.

Computational determination of free (or accessible) volume: Once the optimized geometry of free catalysts (where the catalyst is not bound to the optional R⁴ Lewis base) or coordinated complexes (where a catalyst is bound to the optional R⁴ Lewis base) are obtained using the above method, a sphere of radius 3.0 Å is placed around the B atom (the volume of this sphere is denoted as V1). This is followed by placing spheres on other atoms; the radii of these spheres are chosen to be the van der Waals radii of respective atoms. The volume of the sphere centered on B which is occluded by spheres on other atoms is computed using a Monte Carlo integration technique. The occluded volume is represented as V2. The free volume (FV) is calculated using the following equation:

FV=1−(V2/V1)

The FV descriptor varies between 0 and 1. This technique is implemented using Pipeline Pilot tool kit. This procedure is used in literature to understand bond dissociation trends. 

1. A method of producing a polyether polyol, comprising: reacting a low molecular weight initiator with ethylene oxide in the presence of a polymerization catalyst, the low molecular weight initiator having a nominal hydroxyl functionality at least 2, and the polymerization catalyst being a Lewis acid catalyst having the general formula M(R¹)₁(R²)₁(R³)₁(R⁴)_(0 or 1), whereas M is boron, aluminum, indium, bismuth or erbium, R¹, R², R³, and R⁴ are each independent, R¹ includes a first fluoroalkyl-substituted phenyl group, R² includes a second fluoroalkyl-substituted phenyl group or a first fluoro/chloro-substituted phenyl group, R³ includes a third fluoroalkyl-substituted phenyl group or a second fluoro/chloro-substituted phenyl group, and optional R⁴ includes a functional group or functional polymer group, R¹ being different from at least one of R² and R³; and forming a polyether polyol having a number average molecular weight of greater than the number average molecular weight of the low molecular weight initiator in the presence of the Lewis acid catalyst.
 2. The method as claimed in claim 1, wherein the Lewis acid catalyst has the general formula M(R¹)₁(R²)₁(R³)₁(R⁴)_(0 or 1), whereas R² is the second fluoroalkyl-substituted phenyl group that is the same as first fluoroalkyl-substituted phenyl group, and R³ is the second fluoro/chloro-substituted phenyl group.
 3. The method as claimed in claim 1, wherein the Lewis acid catalyst has the general formula M(R¹)₁(R²)₁(R³)₁(R⁴)_(0 or 1), whereas R² is the second fluoroalkyl-substituted phenyl group that is the same as first fluoroalkyl-substituted phenyl group, and R³ is the third fluoroalkyl-substituted phenyl group that is different from the first fluoroalkyl-substituted phenyl group.
 4. The method as claimed in claim 1, wherein the Lewis acid catalyst has the general formula M(R¹)₁(R²)₁(R³)₁(R⁴)_(0 or 1), whereas R² is the second fluoroalkyl-substituted phenyl group that is different from the first fluoroalkyl-substituted phenyl group, and R³ is the third fluoroalkyl-substituted phenyl group that is different from the first fluoroalkyl-substituted phenyl group and the second fluoroalkyl-substituted phenyl group.
 5. The method as claimed in claim 1, wherein the Lewis acid catalyst has the general formula M(R¹)₁(R²)₁(R³)₁(R⁴)_(0 or 1), whereas R² is the first fluoro/chloro-substituted phenyl group and R³ is the second fluoro/chloro-substituted phenyl group that is that same as the first fluoro/chloro-substituted phenyl group.
 6. The method as claimed in claim 1, wherein the Lewis acid catalyst has the general formula M(R¹)₁(R²)₁(R³)₁(R⁴)_(0 or 1,)whereas at least one of R² and R³ is a fluoro/chloro-fluoroalkyl-substituted phenyl group, difluoro/chloro-fluoroalkyl-substituted phenyl group, trifluoro/chloro-fluoroalkyl-substituted phenyl group, or tetrafluoro/chloro-fluoroalkyl-substituted phenyl group.
 7. The method as claimed in claim 1, wherein the Lewis acid catalyst has the general formula M(R¹)₁(R²)₁(R³)₁(R⁴)_(0 or 1), whereas at least one of R¹, R², and R³ is a 3,4- or 3,5-bis(fluoroalkyl)-substituted phenyl group.
 8. The method as claimed in claim 1, wherein the Lewis acid catalyst has the general formula M(R¹)₁(R²)₁(R³)₁(R⁴)₁.
 9. The method as claimed in claim 8, wherein R⁴ is a cyclic ether having 3-10 carbon atoms.
 10. The method as claimed in claim 8, wherein R⁴ is a ketone having 3-10 carbon atoms.
 11. The method as claimed in claim 1, wherein the polyether polyol has a yield of at least 60% based on actual yield of an ethylene oxide capped polyol and a theoretical yield of the ethylene oxide capped polyol.
 12. The method as claimed in claim 1, wherein the low molecular weight initiator is a polyether diol or triol derived from at least one selected from propylene oxide, ethylene oxide, and butylene oxide.
 13. A method of producing a polyurethane product, the method comprising: providing a polyether polyol produced according to the method as claimed in claim 1, and providing an isocyanate.
 14. A polyether polyol prepared using the method as claimed in claim
 1. 15. A polyurethane product prepared using the polyether polyol as claimed in claim
 14. 